Synthesis and characterization of triphenylamine-containing microporous organic copolymers for carbon dioxide uptake
文献类型：期刊论文
| 作者 | Yang YQ ; Zhang Q ; Zhang SB ; Li SH |
| 刊名 | polymer
 |
| 出版日期 | 2013 |
| 卷号 | 54期号:21页码:5698-5702 |
| 关键词 | HIGH-SURFACE-AREA HYDROGEN STORAGE HYPERCROSSLINKED POLYSTYRENE POLYMER NETWORKS CO2 CAPTURE GAS-STORAGE FRAMEWORKS METHANE ADSORBENTS ADSORPTION |
| ISSN号 | 0032-3861 |
| 通讯作者 | zhang sb |
| 中文摘要 | this article describes the synthesis and characterization of microporous organic copolymers (pp-n-x, where "x" is the molar percent of triphenylamine) prepared from triphenylamine and dichloro-p-xylene using a combination of oxidative polymerization and friedel crafts alkylation process promoted by anhydrous fecl3. the samples possessed bet specific surface areas from 318 to 1530 m(2) g(-1) with the increasing content of dichloro-p-xylene. the highest co2 uptake of 4.60 mmol g(-1) was observed for pp-n-25, which was one of the highest values among mops reported to date under these conditions. the polymers possessed stable and reversible co2 adsorption-desorption performance in at least 5 consecutive runs without noticeable deterioration of co2 uptake capacities. (c) 2013 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000326204200031 |
| 公开日期 | 2014-04-15 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/49549]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Yang YQ,Zhang Q,Zhang SB,et al. Synthesis and characterization of triphenylamine-containing microporous organic copolymers for carbon dioxide uptake[J]. polymer,2013,54(21):5698-5702. |
| APA | Yang YQ,Zhang Q,Zhang SB,&Li SH.(2013).Synthesis and characterization of triphenylamine-containing microporous organic copolymers for carbon dioxide uptake.polymer,54(21),5698-5702. |
| MLA | Yang YQ,et al."Synthesis and characterization of triphenylamine-containing microporous organic copolymers for carbon dioxide uptake".polymer 54.21(2013):5698-5702. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。