Long Chain Bismaleimide Modified Cyanate Ester Resin and Its Composites
文献类型：期刊论文
| 作者 | Ma PC ; Liu JF ; Fan WF ; Meng XS ; Yang M |
| 刊名 | chemical journal of chinese universities-chinese
 |
| 出版日期 | 2013 |
| 卷号 | 34期号:8页码:1979-1984 |
| 关键词 | MOISTURE ABSORPTION MATRICES RATIO |
| ISSN号 | 0251-0790 |
| 通讯作者 | liu jf |
| 中文摘要 | a kind of long chain bismaleimide-modified cyanate ester resin and the relevant composites were prepared and characterized. the results indicate that when the resin content of the long chain maleimide-terminated thioetherimide(mimti) reached 37.5% (mass fraction), the t-5% of the modified cyanate ester resin (mti/t-3) was 414 degrees c. tensile strength and flexural strength of the mti/t-3 composite were 431.2 and 331.0 mpa, 631.5 and 278.4 mpa at room temperature and 200 degrees c, respectively. and its coefficient of thermal expansion(cte) in x-y axis and the moisture absorption were 18.1x10(-6) degrees c-1 and 1.4%, respectively. compared to the common bismaleimide-modified cyanate ester resins, and the 20% and 30% mimti-modified cyanate ester resin mti/t-1 and mti/t-2, respectively, the obtained cyanate ester resin mti/t-3 exhibited good processing, excellent heat resistance and mechanical properties, low moisture absorption and low cte. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 中文 |
| WOS记录号 | WOS:000323357100029 |
| 公开日期 | 2014-04-15 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/49682]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Ma PC,Liu JF,Fan WF,et al. Long Chain Bismaleimide Modified Cyanate Ester Resin and Its Composites[J]. chemical journal of chinese universities-chinese,2013,34(8):1979-1984. |
| APA | Ma PC,Liu JF,Fan WF,Meng XS,&Yang M.(2013).Long Chain Bismaleimide Modified Cyanate Ester Resin and Its Composites.chemical journal of chinese universities-chinese,34(8),1979-1984. |
| MLA | Ma PC,et al."Long Chain Bismaleimide Modified Cyanate Ester Resin and Its Composites".chemical journal of chinese universities-chinese 34.8(2013):1979-1984. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。