Single-crystalline CuGeO3 nanorods: Synthesis, characterization and properties
文献类型：期刊论文
| 作者 | Wang FF ; Xing Y ; Su ZM ; Song SY |
| 刊名 | materials research bulletin
 |
| 出版日期 | 2013 |
| 卷号 | 48期号:7页码:2654-2660 |
| 关键词 | INORGANIC COMPOUND CUGEO3 SPIN-PEIERLS TRANSITION GLASSY-CARBON ELECTRODE PHOTOCATALYTIC PROPERTIES ELECTROCHEMICAL-BEHAVIOR CADMIUM GERMANATE ZN2GEO4 NANORODS ASCORBIC-ACID NANOSTRUCTURES NANOWIRES |
| ISSN号 | 0025-5408 |
| 通讯作者 | xing y |
| 中文摘要 | single crystalline cugeo3 nanorods with a diameter of 20-35 nm and a length up to have been prepared via a facile hydrothermal route with the assistance of ethylenediamine. some influencing factors such as the reaction time, reaction temperature, the volume of ethylenediamine were revealed to play crucial roles in the formation of the cugeo3 nanorods. a possible growth mechanism was proposed based on the experimental results. significantly, this is the first time that cugeo3 was used as a photocatalyst for organic pollutant degradation under uv light irradiation. the reaction constant (k) of cugeo3 nanorods was five times that of the sample prepared by solid-state reaction under uv light irradiation. additionally, the optical and magnetic properties of cugeo3 nanorods were systematically studied. (c) 2013 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000320073600037 |
| 公开日期 | 2014-04-15 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/49763]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang FF,Xing Y,Su ZM,et al. Single-crystalline CuGeO3 nanorods: Synthesis, characterization and properties[J]. materials research bulletin,2013,48(7):2654-2660. |
| APA | Wang FF,Xing Y,Su ZM,&Song SY.(2013).Single-crystalline CuGeO3 nanorods: Synthesis, characterization and properties.materials research bulletin,48(7),2654-2660. |
| MLA | Wang FF,et al."Single-crystalline CuGeO3 nanorods: Synthesis, characterization and properties".materials research bulletin 48.7(2013):2654-2660. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。