Formation of parallel aligned nano-fibrils of a donor-acceptor conjugated copolymer via controlling J-aggregates and post treatment
文献类型：期刊论文
| 作者 | Xu YZ ; Liu JG ; Wang HY ; Yu XH ; Xing RB ; Han YC |
| 刊名 | soft matter
 |
| 出版日期 | 2013 |
| 卷号 | 9期号:41页码:9849-9856 |
| 关键词 | FIELD-EFFECT TRANSISTORS THIN-FILM TRANSISTORS REGIOREGULAR POLY(3-HEXYLTHIOPHENE) EFFECT MOBILITY POLY(3-ALKYLTHIOPHENES) PERFORMANCE DERIVATIVES MORPHOLOGY POLYMERS GROWTH |
| ISSN号 | 1744-683x |
| 通讯作者 | han yc |
| 中文摘要 | we increased the content of j-aggregates in poly[2,5-bis(2-octyldodecyl)pyrrolo[3,4-c]pyrrole-1,4(2h,5h)-dione-alt-2,2' : 5',2 '' : 5 '',2 '''-quaterthiophene](pdqt) solution by choosing appropriate solvents. it was found that the higher content of j-aggregates in solution in good solvents (i.e. cf) led to the formation of parallel aligned nano-fibrils. this morphological transition from the disordered domains to ordered ones could also occur after thermal treatment or solvent vapor annealing. parallel aligned fibrils of pdqt formed in films via annealing at 200 degrees c for 20 min or solvent vapor annealing in a cf atmosphere with a relatively low vapor pressure for 24 hours. in the films filled with parallel aligned fibrils, the pdqt molecules adopted an edge-on orientation and the pi-pi stacking direction of molecules was perpendicular to the growth direction of fibrils. pdqt chains preferred to adopt the extended conformations without chain-folding due to the extremely rigid backbones. the intact conjugation planes of rigid pdqt chains with extended conformations allow the further growth of parallel aligned fibrils, which enhanced the connectivity between crystalline domains. the results in this work are thought to be helpful to improve the charge-carrier transport in pdqt films. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000325372300016 |
| 公开日期 | 2014-04-16 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/50182]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Xu YZ,Liu JG,Wang HY,et al. Formation of parallel aligned nano-fibrils of a donor-acceptor conjugated copolymer via controlling J-aggregates and post treatment[J]. soft matter,2013,9(41):9849-9856. |
| APA | Xu YZ,Liu JG,Wang HY,Yu XH,Xing RB,&Han YC.(2013).Formation of parallel aligned nano-fibrils of a donor-acceptor conjugated copolymer via controlling J-aggregates and post treatment.soft matter,9(41),9849-9856. |
| MLA | Xu YZ,et al."Formation of parallel aligned nano-fibrils of a donor-acceptor conjugated copolymer via controlling J-aggregates and post treatment".soft matter 9.41(2013):9849-9856. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。