REDUCTION KINETICS OF NI(OH)2 TO NICKEL POWDER PREPARATION UNDER HYDROTHERMAL CONDITIONS
文献类型：期刊论文
| 作者 | Yamasaki, N. ; Huanzhen, L. |
| 刊名 | Metallurgical Transactions B-Process Metallurgy
 |
| 出版日期 | 1993 |
| 期号 | 4页码:557-561 |
| 中文摘要 | The reduction kinetics from Ni(OH)2 to fine Ni metal powder under hydrothermal and H-2 pressure conditions using anthraquinon as an activator were investigated. The reduction ratio increased with temperature up to 225-degrees-C. The H-2 molecule was activated by anthraquinone. This activated hydrogen acts as a reduction reagent from Ni2+ to Ni0. The process may proceed by heterogeneous reaction of Ni2+ ion and solid anthraquinon as follows: (1) anthraquinon is hydrated, (2) Ni2+ ion is absorbed on anthraquinon hydride, and (3) this complex decomposes to Ni0 powder, anthraquinon, and H2O. The particle size of nickel powder obtained increased with increasing temperature and with decreasing pH. The average particle size was about 350 nm. The reduction kinetics were in good agreement with a core model equation with surface reaction, that is, 1 - (1 - x)1/3 = kt, where x is a reaction ratio and t is reaction time. Arrhenius plots showed two slopes with activation energies 65.9 kJ/mol at higher temperature and 377.2 kJ/mol at lower one. This result shows that the hydration of anthraquinon and adsorption of Ni2+ ion onto anthraquinon hydride and decomposition to Ni metal and anthraquinone proceed by consecutive reactions and rate determining steps change in each temperature range. |
| 收录类别 | SCI |
| 原文出处 | |
| 语种 | 英语 |
| 公开日期 | 2014-03-14 |
| 版本 | 出版稿 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/7985]  |
| 专题 | 过程工程研究所_研究所（批量导入） |
| 推荐引用方式 GB/T 7714 | Yamasaki, N.,Huanzhen, L.. REDUCTION KINETICS OF NI(OH)2 TO NICKEL POWDER PREPARATION UNDER HYDROTHERMAL CONDITIONS[J]. Metallurgical Transactions B-Process Metallurgy,1993(4):557-561. |
| APA | Yamasaki, N.,&Huanzhen, L..(1993).REDUCTION KINETICS OF NI(OH)2 TO NICKEL POWDER PREPARATION UNDER HYDROTHERMAL CONDITIONS.Metallurgical Transactions B-Process Metallurgy(4),557-561. |
| MLA | Yamasaki, N.,et al."REDUCTION KINETICS OF NI(OH)2 TO NICKEL POWDER PREPARATION UNDER HYDROTHERMAL CONDITIONS".Metallurgical Transactions B-Process Metallurgy .4(1993):557-561. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。