Aggregation-Free Gold Nanoparticles in Ordered Mesoporous Carbons: Toward Highly Active and Stable Heterogeneous Catalysts
文献类型：期刊论文
| 作者 | Wang, Shuai ; Zhao, Qingfei ; Wei, Huimin ; Wang, Jian-Qiang（王建强） ; Cho, Minhyung ; Cho, Hae Sung ; Terasaki, Osamu ; Wan, Ying |
| 刊名 | JOURNAL OF THE AMERICAN CHEMICAL SOCIETY
 |
| 出版日期 | 2013 |
| 卷号 | 135期号:32页码:CONCATENATE(Sheet1!I26,-Sheet1!J26) |
| ISSN号 | 0002-7863 |
| 英文摘要 | A coordination-assisted synthetic approach is reported here for the synthesis of highly active and stable gold nanoparticle catalysts in ordered mesoporous carbon materials using triblock copolymer F127 as a structure-directing agent, thiol-containing silane as a coordination agent, HAuCl4 as a gold source, and phenolic resin as a carbon source. Upon carbonization, the gold precursor becomes reduced to form monodispersed Au nanoparticles of ca. 9.0 nm, which are entrapped or confined by the "rigid" mesoporous carbonaceous framework. Nanoparticle aggregation is inhibited even at a high temperature of 600 degrees C. After removal of the silica component, the materials possess the ordered mesostructure, high surface area (similar to 1800 m(2)/g), large pore volume (similar to 1.19 cm(3)/g), and uniform bimodal mesopore size (<2.0 and 4.0 nm). The monodispersed gold nanoparticles are highly exposed because of the interpenetrated bimodal pores in the carbon framework, which exhibit excellent catalytic performance. A completely selective conversion of benzyl alcohol in water to benzoic acid can be achieved at 90 degrees C and 1 MPa oxygen. Benzyl alcohol can also be quantitatively converted to benzoic acid at 60 degrees C even under an atmospheric pressure, showing great advantages in green chemistry. The catalysts are stable, poison resistant, and reusable with little activity loss due to metal leaching. The silane coupling agent played several functions in this approach: (1) coordinating with gold species by the thiol group to benefit formation of monodispersed Au nanopartides; (2) reacting with phenolic resins by silanol groups to form relatively "rigid" composite framework; (3) pore-forming agent to generate secondary pores in carbon pore walls, which lead to higher surface area, larger pore volumes, and higher accessibility to to the gold nanopartides. Complete removal of the silica component proves to have little effect on the catalytic performance of entrapped Au nanoparticles. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000323241200037 |
| 公开日期 | 2014-06-13 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/13666]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Wang, Shuai,Zhao, Qingfei,Wei, Huimin,et al. Aggregation-Free Gold Nanoparticles in Ordered Mesoporous Carbons: Toward Highly Active and Stable Heterogeneous Catalysts[J]. JOURNAL OF THE AMERICAN CHEMICAL SOCIETY,2013,135(32):CONCATENATE(Sheet1!I26,-Sheet1!J26). |
| APA | Wang, Shuai.,Zhao, Qingfei.,Wei, Huimin.,Wang, Jian-Qiang.,Cho, Minhyung.,...&Wan, Ying.(2013).Aggregation-Free Gold Nanoparticles in Ordered Mesoporous Carbons: Toward Highly Active and Stable Heterogeneous Catalysts.JOURNAL OF THE AMERICAN CHEMICAL SOCIETY,135(32),CONCATENATE(Sheet1!I26,-Sheet1!J26). |
| MLA | Wang, Shuai,et al."Aggregation-Free Gold Nanoparticles in Ordered Mesoporous Carbons: Toward Highly Active and Stable Heterogeneous Catalysts".JOURNAL OF THE AMERICAN CHEMICAL SOCIETY 135.32(2013):CONCATENATE(Sheet1!I26,-Sheet1!J26). |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。