Low-temperature preparation of self-polarized Pb(Mg1/3Nb2/3)O-3-PbTiO3 films on well crystallized LaNiO3 electrodes
文献类型：期刊论文
| 作者 | Zhao, Yuanyuan ; Li, Xiaolong ; Hu, Guangda ; Xu, Jianbin |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2013 |
| 卷号 | 577页码:CONCATENATE(Sheet1!I199,-Sheet1!J199) |
| ISSN号 | 0925-8388 |
| 英文摘要 | 0.68Pb(Mg1/3Nb2/3)O-3-0.32PbTiO(3) (PMN-PT) films were deposited on [100]-oriented LaNiO3 (LNO) electrodes with two different crystallinities by a sal-gel method. A phase-pure PMN-PT film can be formed on the well crystallized LNO electrode at 500 degrees C, 100 degrees C lower than the film deposited on the LNO electrode with lower crystallinity. All the phase-pure PMN-PT films are self-polarized. With the increase of the annealing temperature from 500 to 650 degrees C, the mean piezoelectric coefficient (d(33)) of the films deposited on the well crystallized LNO electrodes increases from 11 to 257 pm/V. This phenomenon is assigned to the defect dipoles and residual stress. (C) 2013 Elsevier B.V. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000324082800099 |
| 公开日期 | 2014-06-13 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/13811]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Zhao, Yuanyuan,Li, Xiaolong,Hu, Guangda,et al. Low-temperature preparation of self-polarized Pb(Mg1/3Nb2/3)O-3-PbTiO3 films on well crystallized LaNiO3 electrodes[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2013,577:CONCATENATE(Sheet1!I199,-Sheet1!J199). |
| APA | Zhao, Yuanyuan,Li, Xiaolong,Hu, Guangda,&Xu, Jianbin.(2013).Low-temperature preparation of self-polarized Pb(Mg1/3Nb2/3)O-3-PbTiO3 films on well crystallized LaNiO3 electrodes.JOURNAL OF ALLOYS AND COMPOUNDS,577,CONCATENATE(Sheet1!I199,-Sheet1!J199). |
| MLA | Zhao, Yuanyuan,et al."Low-temperature preparation of self-polarized Pb(Mg1/3Nb2/3)O-3-PbTiO3 films on well crystallized LaNiO3 electrodes".JOURNAL OF ALLOYS AND COMPOUNDS 577(2013):CONCATENATE(Sheet1!I199,-Sheet1!J199). |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。