Leakage current mechanisms of ultrathin high-k Er2O3 gate dielectric film
文献类型：期刊论文
| 作者 | Wu, Deqi; Yao, Jincheng ; Zhao, Hongsheng; Chang, Aimin; Li, Feng
|
| 刊名 | Journal of Semiconductors
 |
| 出版日期 | 2009 |
| 卷号 | 30期号:10页码:21-26 |
| 关键词 | Er_2O_3 high-kappa gate dielectrics leakage current leakage current mechanisms |
| ISSN号 | 16744926 |
| 通讯作者 | Chang, Aimin |
| 英文摘要 | A series of high dielectric material Er2O3 thin films with different thicknesses were deposited on p-type Si (100) substrate by pulse laser deposition at different temperatures. Phase structures of the films were determined by means of X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). Leakage current density was measured with an HP4142B semiconductor parameter analyzer. The XRD and HRTEM results reveal that Er2O3 thin films deposited below 400 °C are amorphous, while films deposited from 400 to 840 ° are well crystallized with (111)-preferential crystallographic orientation. I-V curves show that, for ultrathin crystalline Er2O3 films, the leakage current density increases by almost one order of magnitude from 6.20 × 10 -5 to 6.56 × 10-4 A/cm2, when the film thickness decreases by only 1.9 nm from 5.7 to 3.8 nm. However the leakage current density of ultrathin amorphous Er2O3 films with a thickness of 3.8 nm is only 1.73 × 10-5 A/cm2. Finally, analysis of leakage current density showed that leakage of ultrathin Er2O3 films at high field is mainly caused by Fowler-Nordheim tunneling, and the large leakage of ultrathin crystalline Er2O3 films could arise from impurity defects at the grain boundary. |
| 收录类别 | EI |
| 公开日期 | 2014-11-11 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/4168]  |
| 专题 | 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | Xinjiang Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Urumqi 830011, China;Institute of Semiconductors, Chinese Academy of Sciences, Beijing 100083, China;Graduate University, Chinese Academy of Sciences, Beijing 100049, China |
| 推荐引用方式 GB/T 7714 | Wu, Deqi,Yao, Jincheng,Zhao, Hongsheng,et al. Leakage current mechanisms of ultrathin high-k Er2O3 gate dielectric film[J]. Journal of Semiconductors,2009,30(10):21-26. |
| APA | Wu, Deqi,Yao, Jincheng,Zhao, Hongsheng,Chang, Aimin,&Li, Feng.(2009).Leakage current mechanisms of ultrathin high-k Er2O3 gate dielectric film.Journal of Semiconductors,30(10),21-26. |
| MLA | Wu, Deqi,et al."Leakage current mechanisms of ultrathin high-k Er2O3 gate dielectric film".Journal of Semiconductors 30.10(2009):21-26. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。