Densi？cation and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti
文献类型：期刊论文
| 作者 | 汤云 ; 张国军 ; 薛佳祥 ; 王新刚 ; 徐常明 ; 黄晓 |
| 刊名 | Journal of the Europpean Ceramic Society
 |
| 出版日期 | 2013-01-24 |
| 期号 | 33页码:1363 |
| ISSN号 | 0955-2219 |
| 其他题名 | Densi？cation and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti |
| 通讯作者 | Guojun Zhang |
| 中文摘要 | The densi？cation of hot-pressed ZrN ceramics doped with Zr or Ti have been investigated at 1500–1700 ？ C. It is shown that either Zr or Ti additive can facilitate the densi？cation process. ZrN with 20 mol% Zr or Ti (named ZNZ and ZNT) sintered at 1700 ？ C can achieve above 98% relative densities whereas densi？cation temperature up to 2000 ？ C is necessary for pure ZrN. The densi？cation improvements are attributed to solid solution of Zr or Ti into ZrN to form non-stoichiometric ZrN1？x or (Zr, Ti)N1？x. The microstructures and mechanical properties of ZNZ and ZNT samples have been examined. Large grain size and ？at fracture surface existed in ZNT sample sintered at 1700 ？ C, which lead to poor toughness as low as 2.3 MPa m1/2 . On the contrary, the fracture toughness of ZNZ sample sintered at 1700 ？ C was up to 5.9 MPa m1/2 , attributed to ？ne and uniform grain size distribution. |
| 学科主题 | 无机陶瓷材料 |
| 语种 | 中文 |
| 公开日期 | 2014-12-18 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/5122]  |
| 专题 | 上海硅酸盐研究所_高性能陶瓷和超微结构国家重点实验室_期刊论文 |
| 推荐引用方式 GB/T 7714 | 汤云,张国军,薛佳祥,等. Densi？cation and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti[J]. Journal of the Europpean Ceramic Society,2013(33):1363. |
| APA | 汤云,张国军,薛佳祥,王新刚,徐常明,&黄晓.(2013).Densi？cation and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti.Journal of the Europpean Ceramic Society(33),1363. |
| MLA | 汤云,et al."Densi？cation and mechanical properties of hot-pressed ZrN ceramics doped with Zr or Ti".Journal of the Europpean Ceramic Society .33(2013):1363. |