热障涂层中在高温服役环境中的微裂纹表征
文献类型：期刊论文
| 作者 | J.J.HUA ; W.WU ; C.C.LIN ; Y.ZENG ; H.WANG99 ; X.B.ZHE |
| 刊名 | Surface Review and Letters
 |
| 出版日期 | 2013-04-11 |
| 期号 | 20页码:1350035 |
| ISSN号 | 0218-625X |
| 其他题名 | MICROCRACKS CHARACTERIZATION FOR THERMAL BARRIER COATINGS AT HIGH TEMPERATURE |
| 通讯作者 | Y. ZENG |
| 中文摘要 | Thermal barrier coatings (TBCs), used in gas turbine blades, are exposed to oxidation and thermal fatigue conditions. The characterization of TBCs was often performed in laboratory experiments, therefore, its detail failure mechanism is not quite obvious. For better understanding of the phenomenon, it is recommended to observe it under the condition simulating the real service conditions of gas turbines. In the present work, ZrO2 coatings were prepared by air plasma spraying (APS). Scanning electron microscope (SEM), equipped with a heating system, was used to study the in situ microstructure change of TBCs at service temperature at which the aircraft is operated. The bond coat (BC) layer's thickening process and thermally grown oxide (TGO) generation along with the cracks growth are revealed. Moreover, the in¡ãuence of the service temperature and holding time on the failure mechanism of TBCs is discussed. The crack healing produced during the coating re-melting reaction is observed, and it is the key factor to increase the thermal conductivity of the coating. |
| 学科主题 | 材料化学 |
| 语种 | 中文 |
| 公开日期 | 2014-12-18 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/4915]  |
| 专题 | 上海硅酸盐研究所_无机材料分析测试中心_期刊论文 |
| 推荐引用方式 GB/T 7714 | J.J.HUA,W.WU,C.C.LIN,等. 热障涂层中在高温服役环境中的微裂纹表征[J]. Surface Review and Letters,2013(20):1350035. |
| APA | J.J.HUA,W.WU,C.C.LIN,Y.ZENG,H.WANG99,&X.B.ZHE.(2013).热障涂层中在高温服役环境中的微裂纹表征.Surface Review and Letters(20),1350035. |
| MLA | J.J.HUA,et al."热障涂层中在高温服役环境中的微裂纹表征".Surface Review and Letters .20(2013):1350035. |