Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain
文献类型：期刊论文
| 作者 | Zhang K(张凯); Zhang K(张坤) ; Li HX(李怀学); Chen GN(陈光南); Zhang K; Zhang K
|
| 刊名 | Journal of Materials Processing Technology
 |
| 出版日期 | 2009 |
| 卷号 | 209期号:3页码:1337-1341 |
| 通讯作者邮箱 | kaizhang@imech.ac.cn; kzhang@imech.ac.cn |
| 关键词 | Electroplated Coating Interface Fracture Compressive Strain T-Bend Test |
| ISSN号 | 0924-0136 |
| 通讯作者 | Zhang K |
| 中文摘要 | The inducement of interface fracture is crucial to the analysis of interfacial adhesion between coating and substrate. For electroplated coating/metal substrate adhering materials with strong adhesion, interface cracking and coating spalling are difficult to be induced by conventional methods. In this paper an improved bending test named as T-bend test was conducted on a model coating system, i.e. electroplated chromium on a steel substrate. After the test, cross-sections of the coated materials were prepared to compare the failure behaviors under tensile strain and compressive strain induced by T-bend test. And the observation results show that coating cracking, interface cracking and partial spalling appear step by step. Based on experimental results, a new method may be proposed to rank the coated materials with strong inter-facial adhesion. (C) 2008 Elsevier B.V. All rights reserved. |
| 类目[WOS] | Engineering, Industrial ; Engineering, Manufacturing ; Materials Science, Multidisciplinary |
| 研究领域[WOS] | Engineering ; Materials Science |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000263394000023 |
| 公开日期 | 2009-08-03 ; 2009-10-09 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/26736]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 通讯作者 | Zhang K; Zhang K |
| 推荐引用方式 GB/T 7714 | Zhang K,Zhang K,Li HX,et al. Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain[J]. Journal of Materials Processing Technology,2009,209(3):1337-1341. |
| APA | 张凯,张坤,李怀学,陈光南,Zhang K,&Zhang K.(2009).Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain.Journal of Materials Processing Technology,209(3),1337-1341. |
| MLA | 张凯,et al."Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain".Journal of Materials Processing Technology 209.3(2009):1337-1341. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。