On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder
文献类型：期刊论文
| 作者 | Chen XJ(陈学军) ; Chen GN(陈光南); Chen XJ
|
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2009 |
| 卷号 | 203期号:9页码:1114-1120 |
| 通讯作者邮箱 | chenxuejuncas@sohu.com |
| 关键词 | Segmented Coating Cracking Thermal Stress Intensity Factor (Tsif) Finite Element Method Thick-Walled Cylinder Barrier Coatings Axial Cracks Shock Fracture Delamination Stability |
| ISSN号 | 0257-8972 |
| 通讯作者 | Chen XJ |
| 中文摘要 | In this work, the thermally induced cracking behavior of a segmented coating has been investigated. The geometry under consideration is a hollow cylinder with a segmented coating deposited onto its outer surface. The segmentation cracks are modeled as a periodic array of axial edge cracks. The finite element method is utilized to obtain the solution of the multiple crack problem and the Thermal Stress Intensity Factors (TSIFs) are calculated. Based on dimensional analysis, the main parameters affecting TSIFs are identified. It has been found that the TSIF is a monotonically increasing function of segmentation crack spacing. This result confirms that a segmented coating exhibits much higher thermal shock resistance than an intact counterpart, if only the segmentation crack spacing is narrow enough. The dependence of TSIF on some other parameters, such as normalized time, segmentation crack depth, convection severity as well as material constants, has also been discussed. (C) 2008 Elsevier B.V. All rights reserved. |
| 类目[WOS] | Materials Science, Coatings & Films ; Physics, Applied |
| 研究领域[WOS] | Materials Science ; Physics |
| 关键词[WOS] | THICK-WALLED CYLINDER ; BARRIER COATINGS ; AXIAL CRACKS ; SHOCK ; FRACTURE ; DELAMINATION ; STABILITY |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000263388200002 |
| 公开日期 | 2009-08-03 ; 2009-10-09 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/26738]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 通讯作者 | Chen XJ |
| 推荐引用方式 GB/T 7714 | Chen XJ,Chen GN,Chen XJ. On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder[J]. Surface & Coatings Technology,2009,203(9):1114-1120. |
| APA | 陈学军,陈光南,&Chen XJ.(2009).On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder.Surface & Coatings Technology,203(9),1114-1120. |
| MLA | 陈学军,et al."On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder".Surface & Coatings Technology 203.9(2009):1114-1120. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。