Preparation of binderless nanopore-isotropic graphite for inhibiting the liquid fluoride salt and Xe-135 penetration for molten salt nuclear reactor
文献类型：期刊论文
| 作者 | Song, JL ; Zhao, YL ; Zhang, JP ; He, XJ ; Zhang, BL ; Lian, PF ; Liu, ZJ ; Zhang, DS ; He, ZT ; Gao, LN ; Xia, HH ; Zhou, XT ; Huai, P ; Guo, QG ; Liu, L |
| 刊名 | CARBON
 |
| 出版日期 | 2014 |
| 卷号 | 79页码:36—45 |
| 关键词 | MESOCARBON-MICROBEADS PYROLYTIC CARBON THERMAL-CONDUCTIVITY RAMAN-SPECTROSCOPY STACKING ORDER INFILTRATION IRRADIATION COMPOSITES FOAMS SEAL |
| ISSN号 | 0008-6223 |
| 通讯作者 | jlsong1982@yeah.net |
| 英文摘要 | Mesocarbon microbeads and the isostatic pressing method were used to prepare binderless nanopore-isotropic graphite (NPIG) as a neutron moderator and reflector, to inhibit liquid fluoride salt and Xe-135 penetration during use in a molten salt nuclear reactor. The microstructure, thermophysical, and other properties of the NPIG were studied and compared with isostatic graphite (IG-110, TOY TANSO CO., Ltd., Japan). A high-pressure reactor and a vacuum device were constructed to evaluate the molten salt and Xe-135 penetration in the graphite, respectively. The results indicated that NPIG possessed a graphitization degree of 74% and excellent properties such as a high bending strength of 94.1 +/- 2.5 MPa, a high compressive strength of 230 +/- 3 MPa, a low porosity of 8.7%, and an average pore diameter of 69 nm. The fluoride salt occupation of IG-110 was 13.5 wt% under 1.5 atm, whereas the salt gain in NPIG remained steady even up to 10 atm with an increase of <0.06 wt%, demonstrating that the graphite could inhibit the liquid fluoride salt infiltration effectively. The helium diffusion coefficient for NPIG was 8.76 x 10(-5) cm(2)/s, much less than 1.21 x 10(-2) cm(2)/s for IG-110. The NPIG could effectively inhibit liquid fluoride salt and Xe-135 penetration. (C) 2014 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000342657100004 |
| 公开日期 | 2015-03-13 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/14326]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Song, JL,Zhao, YL,Zhang, JP,et al. Preparation of binderless nanopore-isotropic graphite for inhibiting the liquid fluoride salt and Xe-135 penetration for molten salt nuclear reactor[J]. CARBON,2014,79:36—45. |
| APA | Song, JL.,Zhao, YL.,Zhang, JP.,He, XJ.,Zhang, BL.,...&Liu, L.(2014).Preparation of binderless nanopore-isotropic graphite for inhibiting the liquid fluoride salt and Xe-135 penetration for molten salt nuclear reactor.CARBON,79,36—45. |
| MLA | Song, JL,et al."Preparation of binderless nanopore-isotropic graphite for inhibiting the liquid fluoride salt and Xe-135 penetration for molten salt nuclear reactor".CARBON 79(2014):36—45. |