The Corrosion Behavior of Pure Iron under Solid Na2SO4 Deposit in Wet Oxygen Flow at 500 degrees C
文献类型：期刊论文
| 作者 | Y. B. Tang ; L. Liu ; L. Fan ; Y. Li ; F. H. Wang |
| 刊名 | Materials
 |
| 出版日期 | 2014 |
| 卷号 | 7期号:9页码:6144-6157 |
| 关键词 | electrochemical reaction Na2SO4 + O-2 + H2O corrosion behavior plus water-vapor nacl deposit hot corrosion oxidation alloys sodium 500-700-degrees-c 600-degrees-c sulfidation nickel |
| ISSN号 | 1996-1944 |
| 原文出处 | |
| 语种 | 英语 |
| 公开日期 | 2015-01-14 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/73387]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. B. Tang,L. Liu,L. Fan,et al. The Corrosion Behavior of Pure Iron under Solid Na2SO4 Deposit in Wet Oxygen Flow at 500 degrees C[J]. Materials,2014,7(9):6144-6157. |
| APA | Y. B. Tang,L. Liu,L. Fan,Y. Li,&F. H. Wang.(2014).The Corrosion Behavior of Pure Iron under Solid Na2SO4 Deposit in Wet Oxygen Flow at 500 degrees C.Materials,7(9),6144-6157. |
| MLA | Y. B. Tang,et al."The Corrosion Behavior of Pure Iron under Solid Na2SO4 Deposit in Wet Oxygen Flow at 500 degrees C".Materials 7.9(2014):6144-6157. |