Remaining life prediction of the core shroud due to stress corrosion cracking failure in BWRs using numerical simulations

文献类型:期刊论文

作者Y. K. ; Lu Li, S. P. ; Li, D. Z. ; Kaji, Y.
刊名Journal of Nuclear Science and Technology
出版日期2015
卷号52期号:1页码:96-103
关键词stress corrosion cracking boiling water reactor life prediction 316L stainless steel finite element methods core shroud
ISSN号0022-3131
原文出处://WOS:000346587100008
公开日期2015-05-08
源URL[http://ir.imr.ac.cn/handle/321006/73852]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Y. K.,Lu Li, S. P.,Li, D. Z.,et al. Remaining life prediction of the core shroud due to stress corrosion cracking failure in BWRs using numerical simulations[J]. Journal of Nuclear Science and Technology,2015,52(1):96-103.
APA Y. K.,Lu Li, S. P.,Li, D. Z.,&Kaji, Y..(2015).Remaining life prediction of the core shroud due to stress corrosion cracking failure in BWRs using numerical simulations.Journal of Nuclear Science and Technology,52(1),96-103.
MLA Y. K.,et al."Remaining life prediction of the core shroud due to stress corrosion cracking failure in BWRs using numerical simulations".Journal of Nuclear Science and Technology 52.1(2015):96-103.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。