Extremely-low-cycle fatigue behaviors of Cu and Cu-Al alloys: Damage mechanisms and life prediction
文献类型：期刊论文
| 作者 | R. ; Zhang Liu, Z. J. ; Zhang, P. ; Zhang, Z. F. |
| 刊名 | Acta Materialia
 |
| 出版日期 | 2015 |
| 卷号 | 83页码:341-356 |
| 关键词 | Extremely-low-cycle fatigue Cyclic hardening Fatigue crack Hysteresis energy Damage mechanism stacking-fault energy ductile crack initiation ultrafine-grained cu microstructural evolution hysteresis energy steel strain deformation assessments transition |
| ISSN号 | 1359-6454 |
| 原文出处 | |
| 公开日期 | 2015-05-08 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/73867]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | R.,Zhang Liu, Z. J.,Zhang, P.,et al. Extremely-low-cycle fatigue behaviors of Cu and Cu-Al alloys: Damage mechanisms and life prediction[J]. Acta Materialia,2015,83:341-356. |
| APA | R.,Zhang Liu, Z. J.,Zhang, P.,&Zhang, Z. F..(2015).Extremely-low-cycle fatigue behaviors of Cu and Cu-Al alloys: Damage mechanisms and life prediction.Acta Materialia,83,341-356. |
| MLA | R.,et al."Extremely-low-cycle fatigue behaviors of Cu and Cu-Al alloys: Damage mechanisms and life prediction".Acta Materialia 83(2015):341-356. |