Catalytic Conversion of Methanol to Propylene over (NH4)(2)SiF6-Modified Nanosized HZSM-5 Zeolite
文献类型：期刊论文
| 作者 | Hu Si1; Zhang Qing1; Xia Zhi2; Gong Yan-Jun1; Xu Jun3; Deng Feng3; Dou Tao1,2 |
| 刊名 | ACTA PHYSICO-CHIMICA SINICA
 |
| 出版日期 | 2012-11-01 |
| 卷号 | 28期号:11页码:2705-2712 |
| 关键词 | Nanosized ZSM-5 Dealumination Pore structure Acidity Propylene selectivity Catalytic lifespan |
| 英文摘要 | (NH4)(2)SiF6-modified nanosized HZSM-5 zeolite was prepared and investigated as a catalyst for methanol to propylene conversion. The effects of this modification on the framework, textural properties and acidity of both the parent and the modified HZSM-5 zeolite were investigated by powder X-ray diffraction (XRD), Al-27 magic angle spinning nuclear magnetic resonance (Al-27 MAS NMR), X-ray fluorescence (XRF), X-ray photoelectron spectroscopy (XPS), N-2 adsorption, transmission electron microscopy (TEM), temperature-programmed desorption of ammonia (NH3-TPD), and infrared spectroscopy of adsorbed pyridine (Py-IR). The catalytic performance of these materials on the methanol to propylene (MTP) conversion process was tested under operating conditions of T=450 degrees C, p=0.1 MPa (p(MeOH)=50 kPa) and WHSV=1 h(-1). The results showed that surface aluminum on the nanosized ZSM-5 zeolite could be selectively removed by the (NH4)(2)SiF6 solution and that the number of acidic sites on the HZSM-5 zeolite gradually decreased with increasing (NH4)(2)SiF6 concentration. Moreover, after modification with an optimally concentrated (NH4)(2)SiF6 solution, an obvious increase in specific surface area as well as mesopore volume was observed for the nanosized HZSM-5 with a resulting dramatic improvement in the catalytic performance of this material for the MTP reaction. Both the propylene selectivity and propylene/ethylene (PIE) mass ratio resulting from use of the modified HZSM-5 increased significantly to 45.1% and 8.0, as compared to results of 28.8% and 2.6 obtained with the original material. In addition, the catalytic lifespan of the modified zeolite was double that of the original. |
| WOS标题词 | Science & Technology ; Physical Sciences |
| 类目[WOS] | Chemistry, Physical |
| 研究领域[WOS] | Chemistry |
| 关键词[WOS] | HIGH-SILICA HZSM-5 ; H-ZSM-5 ; PERFORMANCE ; ACIDITY ; PROPENE ; DEALUMINATION ; HYDROCARBONS ; MESOPOROSITY ; SINGLE ; ZSM-5 |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000311597200025 |
| 公开日期 | 2015-07-14 |
| 源URL | [http://ir.wipm.ac.cn/handle/112942/1640]  |
| 专题 | 武汉物理与数学研究所_磁共振应用研究部 |
| 作者单位 | 1.China Univ Petr, Key Lab Catalysis CNPC, Beijing 102249, Peoples R China 2.Taiyuan Univ Technol, Inst Special Chem, Taiyuan 030024, Peoples R China 3.Chinese Acad Sci, Wuhan Inst Phys & Math, Wuhan 430071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Hu Si,Zhang Qing,Xia Zhi,et al. Catalytic Conversion of Methanol to Propylene over (NH4)(2)SiF6-Modified Nanosized HZSM-5 Zeolite[J]. ACTA PHYSICO-CHIMICA SINICA,2012,28(11):2705-2712. |
| APA | Hu Si.,Zhang Qing.,Xia Zhi.,Gong Yan-Jun.,Xu Jun.,...&Dou Tao.(2012).Catalytic Conversion of Methanol to Propylene over (NH4)(2)SiF6-Modified Nanosized HZSM-5 Zeolite.ACTA PHYSICO-CHIMICA SINICA,28(11),2705-2712. |
| MLA | Hu Si,et al."Catalytic Conversion of Methanol to Propylene over (NH4)(2)SiF6-Modified Nanosized HZSM-5 Zeolite".ACTA PHYSICO-CHIMICA SINICA 28.11(2012):2705-2712. |
入库方式： OAI收割
来源：武汉物理与数学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。