Fabrication of SrTiO3 Nanocrystalline Film Photoelectrode and Its Photoelectrochemical Anticorrosion Properties for Stainless Steel
文献类型：期刊论文
| 作者 | Bu Yu-Yu2,3; Li Wei-Bing2; Yu Jian-Qiang1; Wang Xiu-Tong3; Qi Mei-Ling2; Nie Meng-Yan4; Hou Bao-Rong3 |
| 刊名 | ACTA PHYSICO-CHIMICA SINICA
 |
| 出版日期 | 2011-10-01 |
| 卷号 | 27期号:10页码:2393-2399 |
| 关键词 | SrTiO3 Film photoelectrode Photoelectrochemistry Corrosion and protection 304 stainless steel |
| 英文摘要 | The photoelectrochemical properties of a SrTiO3 film coated on an indium-tin oxide (ITO) conducting glass were investigated for the anticorrosion of 304 stainless steel (304SS) under solar light illumination. The SrTiO3 nanocrystal powders were synthesized using a sol-gel process in the absence and presence of the cetyltrimethyl ammonium bromide (CTAB) surfactant and characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was showed that the as-synthesized SrTiO3 materials exhibit a single perovskite structure and the presence of CTAB leads to uniform particles with an average size of 90 nm. The UV-Vis diffuse reflectance analysis shows that both SrTiO3 films that were prepared in the absence and presence of CTAB surfactant absorbs strongly in the UV region with an absorption threshold edge near 380 nm while the SiTiO3 prepared in the presence of CTAB exhibited a stronger absorption in the UV region than those in the absence of CTAB. The photo-electrochemical anticorrosion effects of SrTiO3 on 304 stainless steel substrates in a 0.5 mol.L-1 NaCl solution were investigated using a 0.1 mol.L-1 NaOH and 0.2 mol.L-1 Na2S hole sacrifice electrolyte solution. Metallographic images of the 304 stainless steel before and after immersion in a 0.5 mol.L-1 NaCl+0.05 mol.L-1 HCl solution for 6 h demonstrates that the SrTiO3 film coated photoelectrode exhibits excellent photoelectrochemical anticorrosion performance on 304 stainless steel. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000295380300021 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/32940]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.Qingdao Univ 266071, Key Lab New Fiber Mat & Modern Text, Qingdao, Shandong, Peoples R China 2.Qingdao Univ Sci & Technol, Fac Environm & Safety, Qingdao 266042, Shandong, Peoples R China 3.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Shandong, Peoples R China 4.Univ Southampton, Natl Ctr Adv Tribol Southampton, Sch Engn Sci, Southampton, Hants, England |
| 推荐引用方式 GB/T 7714 | Bu Yu-Yu,Li Wei-Bing,Yu Jian-Qiang,et al. Fabrication of SrTiO3 Nanocrystalline Film Photoelectrode and Its Photoelectrochemical Anticorrosion Properties for Stainless Steel[J]. ACTA PHYSICO-CHIMICA SINICA,2011,27(10):2393-2399. |
| APA | Bu Yu-Yu.,Li Wei-Bing.,Yu Jian-Qiang.,Wang Xiu-Tong.,Qi Mei-Ling.,...&Hou Bao-Rong.(2011).Fabrication of SrTiO3 Nanocrystalline Film Photoelectrode and Its Photoelectrochemical Anticorrosion Properties for Stainless Steel.ACTA PHYSICO-CHIMICA SINICA,27(10),2393-2399. |
| MLA | Bu Yu-Yu,et al."Fabrication of SrTiO3 Nanocrystalline Film Photoelectrode and Its Photoelectrochemical Anticorrosion Properties for Stainless Steel".ACTA PHYSICO-CHIMICA SINICA 27.10(2011):2393-2399. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。