Transparent alumina fabricated by SPS sintering with AlF3 doping
文献类型：期刊论文
| 作者 | Wang, Dewen ; Shen, Lu ; Ran, Songlin ; Huang, Qing |
| 刊名 | SCRIPTA MATERIALIA
 |
| 出版日期 | 2014 |
| 卷号 | 92页码:31 |
| 中文摘要 | Transparent alumina was fabricated by spark plasma sintering with AlF3 doping at a high heating rate of 100 degrees C min(-1) and a moderate loading pressure of 73 MPa. The sintered AlF3-doped alumina was dark in color due to light absorption by F- substitution and by the resulting defects induced in the alumina lattice. An AlF3 doping concentration of 0.1% was found best for producing transparent alumina. A possible mechanism was proposed to explain the doping effect under the present sintering condition. (C) 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
| 公开日期 | 2015-09-20 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/11671]  |
| 专题 | 宁波材料技术与工程研究所_2014专题 |
| 推荐引用方式 GB/T 7714 | Wang, Dewen,Shen, Lu,Ran, Songlin,et al. Transparent alumina fabricated by SPS sintering with AlF3 doping[J]. SCRIPTA MATERIALIA,2014,92:31. |
| APA | Wang, Dewen,Shen, Lu,Ran, Songlin,&Huang, Qing.(2014).Transparent alumina fabricated by SPS sintering with AlF3 doping.SCRIPTA MATERIALIA,92,31. |
| MLA | Wang, Dewen,et al."Transparent alumina fabricated by SPS sintering with AlF3 doping".SCRIPTA MATERIALIA 92(2014):31. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。