Low-Temperature Synthesis of Nanocrystalline NbB2 Powders by Borothermal Reduction in Molten Salt
文献类型：期刊论文
| 作者 | Ran, Songlin ; Sun, Huifeng ; Wei, Ya'nan ; Wang, Dewen ; Zhou, Niming ; Huang, Qing |
| 刊名 | JOURNAL OF THE AMERICAN CERAMIC SOCIETY
 |
| 出版日期 | 2014 |
| 卷号 | 97期号:11页码:3384 |
| 中文摘要 | Nanocrystalline NbB2 powders were successfully prepared by borothermal reduction in molten salt at 800 degrees C-1000 degrees C. Due to the more homogeneous mixing and more rapid diffusion of species in the liquid state than in the solid state, the synthesis temperature of pure NbB2 phase was greatly decreased by the presence of molten NaCl/KCl salt. The NbB2 powders synthesized at 1000 degrees C had the largest specific surface area of 27.09m(2)/g and the lowest equivalent average particle size of 32nm, respectively. |
| 公开日期 | 2015-09-20 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/11700]  |
| 专题 | 宁波材料技术与工程研究所_2014专题 |
| 推荐引用方式 GB/T 7714 | Ran, Songlin,Sun, Huifeng,Wei, Ya'nan,et al. Low-Temperature Synthesis of Nanocrystalline NbB2 Powders by Borothermal Reduction in Molten Salt[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2014,97(11):3384. |
| APA | Ran, Songlin,Sun, Huifeng,Wei, Ya'nan,Wang, Dewen,Zhou, Niming,&Huang, Qing.(2014).Low-Temperature Synthesis of Nanocrystalline NbB2 Powders by Borothermal Reduction in Molten Salt.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,97(11),3384. |
| MLA | Ran, Songlin,et al."Low-Temperature Synthesis of Nanocrystalline NbB2 Powders by Borothermal Reduction in Molten Salt".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 97.11(2014):3384. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。