Synthesis of B4C-TiB2 composite powders by the carbide boronizing process
文献类型：期刊论文
| 作者 | Wang, Dewen ; Sun, Huifeng ; Deng, Qihuang ; Ding, Zhihui ; Ran, Songlin ; Huang, Qing |
| 刊名 | CERAMICS INTERNATIONAL
 |
| 出版日期 | 2014 |
| 卷号 | 40期号:9页码:15341 |
| 中文摘要 | B4C-TiB2 composite powders were synthesized by a carbide boronizing process, i.e. the solid state reaction between TiC and amorphous boron powders. The particle size of the raw TiC powders was found to greatly affect the phase composition of the composite powders. Nano-TiC powders could be totally consumed and turned into TiB2 phase with heat treatment at 1100 degrees C for 1 h whereas micro-TiC powders was still present even at 1400 degrees C for 1 h. The synthesized B4C-TiB2 composite powders have a small particle size and a homogenous phase distribution, indicating high sintering activity. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 公开日期 | 2015-09-20 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/11713]  |
| 专题 | 宁波材料技术与工程研究所_2014专题 |
| 推荐引用方式 GB/T 7714 | Wang, Dewen,Sun, Huifeng,Deng, Qihuang,et al. Synthesis of B4C-TiB2 composite powders by the carbide boronizing process[J]. CERAMICS INTERNATIONAL,2014,40(9):15341. |
| APA | Wang, Dewen,Sun, Huifeng,Deng, Qihuang,Ding, Zhihui,Ran, Songlin,&Huang, Qing.(2014).Synthesis of B4C-TiB2 composite powders by the carbide boronizing process.CERAMICS INTERNATIONAL,40(9),15341. |
| MLA | Wang, Dewen,et al."Synthesis of B4C-TiB2 composite powders by the carbide boronizing process".CERAMICS INTERNATIONAL 40.9(2014):15341. |