Evolution and effects of surface degradation layer of Sm2Co17 magnets at high temperatures
文献类型：期刊论文
| 作者 | Mao, Shoudong ; Yan, Minsheng ; Nie, Xia ; Sun, Keqing ; Jiang, Jianjun ; Song, Zhenlun |
| 刊名 | JOURNAL OF APPLIED PHYSICS
 |
| 出版日期 | 2014 |
| 卷号 | 115期号:4 |
| 中文摘要 | The long-term application of SmCo-based magnets at high temperatures has been restricted by the irreversible loss of magnetic properties. In this work, degradation behavior of Sm2Co17 magnets was studied at 500 degrees C in air and vacuum by being focused on the surface degradation layer. The structure and the composition of the degradation layer were studied experimentally, and the magnetization was calculated to certify the deduction of the irreversible loss. The soft magnetic phases in the degradation layer can result in the decline of the magnetization and the irreversible loss of magnetic properties. Furthermore, the controversial formation reason of the degradation layer was also studied. It was found that the diffusion of the oxygen, but not the sublimation of Sm, could be the dominant formation reason of the degradation layers. (C) 2014 AIP Publishing LLC. |
| 公开日期 | 2015-09-20 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/11954]  |
| 专题 | 宁波材料技术与工程研究所_2014专题 |
| 推荐引用方式 GB/T 7714 | Mao, Shoudong,Yan, Minsheng,Nie, Xia,et al. Evolution and effects of surface degradation layer of Sm2Co17 magnets at high temperatures[J]. JOURNAL OF APPLIED PHYSICS,2014,115(4). |
| APA | Mao, Shoudong,Yan, Minsheng,Nie, Xia,Sun, Keqing,Jiang, Jianjun,&Song, Zhenlun.(2014).Evolution and effects of surface degradation layer of Sm2Co17 magnets at high temperatures.JOURNAL OF APPLIED PHYSICS,115(4). |
| MLA | Mao, Shoudong,et al."Evolution and effects of surface degradation layer of Sm2Co17 magnets at high temperatures".JOURNAL OF APPLIED PHYSICS 115.4(2014). |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。