Reconstructed PtFe Alloy Nanoparticles with Bulk-Surface Differential Structure for Methanol Oxidation
文献类型：期刊论文
| 作者 | Lv, Qing ; Xiao, Yao ; Yin, Min ; Ge,Junjie ; Xing,Wei ; Liu Changpeng |
| 刊名 | electrochimica acta
 |
| 出版日期 | 2014 |
| 卷号 | 139期号:10页码:61-68 |
| 关键词 | ELECTROCATALYTIC OXIDATION ANODE CATALYST FUEL-CELLS ELECTROOXIDATION RU REDUCTION TOLERANCE COMPOSITE PLATINUM PTRU/C |
| 通讯作者 | ge,jj |
| 英文摘要 | the high cost of the catalyst material is a large obstacle for the commercialization of direct methanol fuel cells. in present work, the non-noble metal fe was added to the conventional pt/c catalyst in order to lowering the catalyst cost without sacrificing the catalytic performance. a chemically dealloying procedure was adopted to leach out the surface iron atoms and thereby increasing the stability of the catalyst. through these procedures, the ptfe bulk-surface differential nano-catalyst was obtained. the shift in diffraction angles according to xrd spectra confirms the formation of the alloy structure between pt and fe. tem results indicate that the chemically dealloyed ptfe/c nanoparticles are uniformly-dispersed with optimized average size. the ptfe bulk-surface differential structure is inferred from xps as no surface fe atoms are detected in spite of the change in pt electronic structure. the existence of fe atoms inside the nanoparticles is further confirmed by the icp characterization. electrochemical characterizations show that the catalytic activity is increased to 2.8 times, compared to the pt/c catalyst, which can be ascribed to the electronic effect of fe. a further evidence for the electronic effect comes from the co stripping spectroscopy, in which the onset potential for co oxidation shifts dramatically toward the negative potential side compared with pt/c. owing to the bulk-surface differential structure, the chemically dealloyed ptfe/c catalysts exhibits nearly the same stability compared to that of the pt/c catalyst. (c) 2014 elsevier ltd. all rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000342275200010 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/56254]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Lv, Qing,Xiao, Yao,Yin, Min,et al. Reconstructed PtFe Alloy Nanoparticles with Bulk-Surface Differential Structure for Methanol Oxidation[J]. electrochimica acta,2014,139(10):61-68. |
| APA | Lv, Qing,Xiao, Yao,Yin, Min,Ge,Junjie,Xing,Wei,&Liu Changpeng.(2014).Reconstructed PtFe Alloy Nanoparticles with Bulk-Surface Differential Structure for Methanol Oxidation.electrochimica acta,139(10),61-68. |
| MLA | Lv, Qing,et al."Reconstructed PtFe Alloy Nanoparticles with Bulk-Surface Differential Structure for Methanol Oxidation".electrochimica acta 139.10(2014):61-68. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。