Preparation and characterization of novel positively charged copolymer composite membranes for nanofiltration
文献类型：期刊论文
| 作者 | Dong, Xue ; Li, Shenghai ; Zhang, Qifeng ; Zhang,Suobo |
| 刊名 | rsc advances
 |
| 出版日期 | 2014 |
| 卷号 | 4期号:43页码:22625-22631 |
| 关键词 | POLY(ETHER ETHER KETONE) INTERFACIAL POLYMERIZATION REVERSE-OSMOSIS WATER-TREATMENT CROSS-LINKING WASTE-WATER REMOVAL PERFORMANCE RETENTION CHLORIDE |
| 通讯作者 | zhang,qf |
| 英文摘要 | a novel copolymer poly(ether ether ketone) bearing pendant tertiary amine groups (tapeek-x) was synthesized by 3,3'-dimethylaminemethylene-4,4'-biphenol (dabp), 4,4'-bisfluorodiphenylketone (bfdpa) and bisphenol a (bpa). after reaction with iodomethane, the copolymer turned to poly(ether ether ketone) with pendant quaternary ammonium groups (qapeek-x). afterward, qapeek-x copolymer was dissolved in formic acid and coated on pan ultrafiltration membrane as a composite membrane. the nf membrane preparation conditions, such as drying temperature, formic acid concentration, copolymer concentration, feed concentration, and tolerance in chlorine solution were investigated. the experiments showed that the membrane whose coating polymer concentration was 0.5 wt% in 88% formic acid had the best flux of 12.6 l m (2) h (1) at 0.4 mpa and best rejection of 99.4% for 500 ppm mgcl2. in addition, the membrane showed excellent tolerance ability of chlorine with a little decrease of mgcl2 rejection. to some extent, this study provides a new insight to improve membrane separation capability and stability in the desalination process. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000337124900047 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/57267]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Dong, Xue,Li, Shenghai,Zhang, Qifeng,et al. Preparation and characterization of novel positively charged copolymer composite membranes for nanofiltration[J]. rsc advances,2014,4(43):22625-22631. |
| APA | Dong, Xue,Li, Shenghai,Zhang, Qifeng,&Zhang,Suobo.(2014).Preparation and characterization of novel positively charged copolymer composite membranes for nanofiltration.rsc advances,4(43),22625-22631. |
| MLA | Dong, Xue,et al."Preparation and characterization of novel positively charged copolymer composite membranes for nanofiltration".rsc advances 4.43(2014):22625-22631. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。