Polystyrene Microbeads by Dispersion Polymerization: Effect of Solvent on Particle Morphology
文献类型:期刊论文
作者 | Lei Jinhua ; Zhou Guangyuan |
刊名 | international journal of polymer science
![]() |
出版日期 | 2014 |
页码 | 703205 |
关键词 | SUSPENSION POLYMERIZATION EMULSION POLYMERIZATION POLAR-SOLVENTS STYRENE SIZE MECHANISMS |
通讯作者 | zhou,gy |
英文摘要 | polystyrene microspheres (ps) were synthesized by dispersion polymerization in ethanol/2-methoxyethanol (etoh/egme) blend solvent using styrene (st) as monomer, azobisisobutyronitrile (aibn) as initiator, and pvp (polyvinylpyrrolidone) k-30 as stabilizer. the typical recipe of dispersion polymerization is as follows: st/solvent/aibn/pvp = 10 g/88 g/0.1 g/2 g. the morphology of polystyrene microspheres was characterized by the scanning electron microscopy (sem) and the molecular weights of ps particles were measured by the ubbelohde viscometer method. the effect of ethanol content in the blend solvent on the morphology and molecular weight of polystyrene was studied. we found that the size of polystyrene microspheres increased and the molecular weight of polystyrene microspheres decreased with the decreasing of the ethanol content in the blend solvent from 100 wt% to 0 wt%. what is more, the size monodispersity of polystyrene microspheres was quite good when the pure ethanol or pure 2-methoxyethanol was used; however when the blend ethanol/2-methoxyethanol solvent was used, the polystyrene microspheres became polydisperse. we further found that the monodispersity of polystyrene microspheres can be significantly improved by adding a small amount of water into the blend solvent; the particles became monodisperse when the content of water in the blend solvent was up to 2 wt%. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000330483600001 |
源URL | [http://ir.ciac.jl.cn/handle/322003/57521] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Lei Jinhua,Zhou Guangyuan. Polystyrene Microbeads by Dispersion Polymerization: Effect of Solvent on Particle Morphology[J]. international journal of polymer science,2014:703205. |
APA | Lei Jinhua,&Zhou Guangyuan.(2014).Polystyrene Microbeads by Dispersion Polymerization: Effect of Solvent on Particle Morphology.international journal of polymer science,703205. |
MLA | Lei Jinhua,et al."Polystyrene Microbeads by Dispersion Polymerization: Effect of Solvent on Particle Morphology".international journal of polymer science (2014):703205. |
入库方式: OAI收割
来源:长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。