New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature
文献类型：期刊论文
| 作者 | Shao, ZP; Xiong, GX; Sheng, SS; Chen, HR; Li, L; Delmon, B; Jacobs, PA; Maggi, R; Martens, JA; Grange, P |
| 刊名 | preparation of catalysts vii
 |
| 出版日期 | 1998 |
| 卷号 | 118页码:431-439 |
| 英文摘要 | a pure phase perovskite-type composite oxide la0.8sr0.2coo3 (lsco) was prepared by three methods: sol-gel method using edta as ligand, environmentaly safe metal-edta-cellulose complexing method and metal-citric-cellulose complexing method. the formation processes of lsco by those methods were investigated by tg-dta, xrd and ir spectroscopy. the results indicated that when edta complexing method was used, at optimized condition, pure phase perovskite-type lsco was acquired after the precursor was fired at 800 degrees c for 2hr. in the process of forming perovskite lsco, srco3 was formed and calcination temperatures higher than 800 degrees c was needed to get rid of it, similar to the citric complexing method reported. when cellulose was introduced, the minimum calcination temperature to acquire pure phase lsco was significantly lowered to around 600 degrees c for metal-edta-cellulose method and 540 degrees c for metal-citric-cellulose method. low calcination temperature led to relatively high bet area for 21m(2)/g and 22m(2)/g respectively. but the surface area were significantly reduced to 12.7m(2)/g and 12.1m(2)/g respectively when they were further fired at 620 degrees c for 2hr. |
| WOS标题词 | science & technology ; physical sciences |
| 类目[WOS] | chemistry, physical |
| 研究领域[WOS] | chemistry |
| 关键词[WOS] | oxygen permeation ; oxides ; decomposition |
| 收录类别 | ISTP ; SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000076264000047 |
| 公开日期 | 2015-11-10 |
| 源URL | [http://159.226.238.44/handle/321008/138135]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China |
| 推荐引用方式 GB/T 7714 | Shao, ZP,Xiong, GX,Sheng, SS,et al. New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature[J]. preparation of catalysts vii,1998,118:431-439. |
| APA | Shao, ZP.,Xiong, GX.,Sheng, SS.,Chen, HR.,Li, L.,...&Poncelet, G.(1998).New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature.preparation of catalysts vii,118,431-439. |
| MLA | Shao, ZP,et al."New methods to prepare perovskite-type La0.8Sr0.2CoO3 catalyst at low temperature".preparation of catalysts vii 118(1998):431-439. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。