CO selective oxidation in H-2-rich gas over Ag nanoparticles - effect of oxygen treatment temperature on the activity of silver particles mechanically mixed with SiO2
文献类型：期刊论文
| 作者 | Qu, ZP; Cheng, MJ; Dong, XL; Bao, XH |
| 刊名 | catalysis today
 |
| 出版日期 | 2004-09-01 |
| 卷号 | 93-5页码:247-255 |
| 关键词 | CO selective oxidation silver powder SiO2 mechanical mixing oxygen treatment |
| 英文摘要 | in order to elucidate the roles of pretreatment with oxygen at high temperatures and the interaction between ag nanoparticles and sio2 in low-temperature co selective oxidation, a mechanical mixture of ag nanoparticles and sio2 powder was prepared and pretreated with oxygen at different temperatures. the samples calcined at 300 and 400 degreesc have poor activities for co oxidation, while oxygen reacts totally with h-2 at temperatures of 160 and 120 degreesc, respectively. it becomes catalytically active after treatment with oxygen at 500 degreesc, and the activity increases with the treatment temperature up to 700 degreesc, reaching nearly the same level of co conversion as that of the 8%ag/sio2 prepared by the incipient wetness impregnation method and treated with he at 500 degreesc. xrd and tem results show that calcinations under oxygen atmosphere between 500 and 700 degreesc help dispersing the silver nanoparticles on the surface of sio2, as well as induce an interaction between the silver nanoparticles and sio2. moreover, the ability of co adsorption at low temperatures is obviously enhanced. however, further increasing the pretreatment temperature decreases the catalytic activity due to the heat-induced aggregation of silver nanoparticles on the surface of sio2 and the corresponding decrease of the co adsorption ability, but higher than that of the initial ag-sio2 mixture. co adsorbed on the ag nanoparticles dispersed on the surface of silica shows a high activity toward co selective oxidation, and it is proved that the sub-surface oxygen species plays a very important role in this reaction. (c) 2004 published by elsevier b.v. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
| 研究领域[WOS] | chemistry ; engineering |
| 关键词[WOS] | noble-metal catalysts ; carbon-monoxide ; films |
| 收录类别 | ISTP ; SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000223973200034 |
| 公开日期 | 2015-11-10 |
| 源URL | [http://159.226.238.44/handle/321008/138435]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, State Key Lab Catalysis, Dalian 116023, Peoples R China 2.Dalian Univ Technol, Dalian 116024, Peoples R China |
| 推荐引用方式 GB/T 7714 | Qu, ZP,Cheng, MJ,Dong, XL,et al. CO selective oxidation in H-2-rich gas over Ag nanoparticles - effect of oxygen treatment temperature on the activity of silver particles mechanically mixed with SiO2[J]. catalysis today,2004,93-5:247-255. |
| APA | Qu, ZP,Cheng, MJ,Dong, XL,&Bao, XH.(2004).CO selective oxidation in H-2-rich gas over Ag nanoparticles - effect of oxygen treatment temperature on the activity of silver particles mechanically mixed with SiO2.catalysis today,93-5,247-255. |
| MLA | Qu, ZP,et al."CO selective oxidation in H-2-rich gas over Ag nanoparticles - effect of oxygen treatment temperature on the activity of silver particles mechanically mixed with SiO2".catalysis today 93-5(2004):247-255. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。