Electrocatalytic property of Pt-Sn anode catalyst for electro-oxidation of ethanol
文献类型：期刊论文
| 作者 | Zhao, XS; Jiang, LH; Sun, GQ; Yang, SH; Yi, BL; Xin, Q |
| 刊名 | chinese journal of catalysis
 |
| 出版日期 | 2004-12-01 |
| 卷号 | 25期号:12页码:983-988 |
| 关键词 | direct ethanol fuel cell platinum tin alternating current impedance method fuel crossover |
| 英文摘要 | ethanol was used as an anode fuel for polymer electrolyte fuel cells, and the electro-oxidation of ethanol on pt-sn/c and pt-ru/c was investigated by voltammetry and alternating current impedance method. the apparent diffusion coefficients of ethanol and methanol through the nafion 117 membrane at different temperatures were compared. it was found that the apparent diffusion coefficient of ethanol was lower than that of methanol under the same condition. the temperature dependence of ethanol electro-oxidation property on pt-sn/ c and pt-ru/c electrode was conducted by voltammetry method. in the temperature range of 30similar to90 degreesc .the pt-sn/c showed superior electrocatalytic property comparing with pt-ru/c. for example, the onset potential of pt-sn/c electrode was approximately 0.2 v lower than that of pt-ru/c at the tested temperatures. at the same potential, the current density of ethanol electro-oxidation on pt-sn/c electrode was about 20-60 ma/cm(2) higher than that on pt-ru/c, and the value difference increased with the increase of temperature. impedance measurements were carried out to interpret the reaction mechanism of ethanol electro-oxidation. the result showed that pt-sn/c had higher catalytic activity for ethanol oxidation. in addition, the direct ethanol fuel cells with pt-sn/c electrode exhibited better performance, the peak power density was 44 mw/cm(2), and it was only 27 mw/cm(2) for single cell with pt-ru/c electrode using oxygen as oxidant at 90 degreesc. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
| 研究领域[WOS] | chemistry ; engineering |
| 关键词[WOS] | methanol fuel-cells ; ac-impedance spectroscopy ; co-tolerance ; oxidation ; electrode ; platinum ; temperature ; performance ; mechanism ; dafc |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000226325900012 |
| 公开日期 | 2015-11-10 |
| 源URL | [http://159.226.238.44/handle/321008/138440]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhao, XS,Jiang, LH,Sun, GQ,et al. Electrocatalytic property of Pt-Sn anode catalyst for electro-oxidation of ethanol[J]. chinese journal of catalysis,2004,25(12):983-988. |
| APA | Zhao, XS,Jiang, LH,Sun, GQ,Yang, SH,Yi, BL,&Xin, Q.(2004).Electrocatalytic property of Pt-Sn anode catalyst for electro-oxidation of ethanol.chinese journal of catalysis,25(12),983-988. |
| MLA | Zhao, XS,et al."Electrocatalytic property of Pt-Sn anode catalyst for electro-oxidation of ethanol".chinese journal of catalysis 25.12(2004):983-988. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。