Studies on the membrane strength of alginate/chitosan microcapsule prepared by emulsification/internal gelation method
文献类型：期刊论文
| 作者 | Liu, Q; Xue, WM; Yu, WT; Liu, XD |
| 刊名 | chemical journal of chinese universities-chinese
 |
| 出版日期 | 2002-07-01 |
| 卷号 | 23期号:7页码:1417-1420 |
| 关键词 | alginate chitosan microcapsule emulsification internal gelation |
| 英文摘要 | the alginate/chitosan microcapsule was prepared by emulsification/internal gelation method. it was found that the membrane strength was significantly affected by the molecular weight of chitosan, reaction time of these two polymers and the ph value of chitosan solution. when the molecular weight of chitosan was lower than 0.1 million, reaction time was higher than 15 min, ph of chitosan solution was about 6.0, then the most strongest membrane was obtained. at the same time the principle of the reaction of polyelectrolyte complexation was investigated. |
| WOS标题词 | science & technology ; physical sciences |
| 类目[WOS] | chemistry, multidisciplinary |
| 研究领域[WOS] | chemistry |
| 关键词[WOS] | release |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000176908400051 |
| 公开日期 | 2015-11-10 |
| 源URL | [http://159.226.238.44/handle/321008/139088]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Q,Xue, WM,Yu, WT,et al. Studies on the membrane strength of alginate/chitosan microcapsule prepared by emulsification/internal gelation method[J]. chemical journal of chinese universities-chinese,2002,23(7):1417-1420. |
| APA | Liu, Q,Xue, WM,Yu, WT,&Liu, XD.(2002).Studies on the membrane strength of alginate/chitosan microcapsule prepared by emulsification/internal gelation method.chemical journal of chinese universities-chinese,23(7),1417-1420. |
| MLA | Liu, Q,et al."Studies on the membrane strength of alginate/chitosan microcapsule prepared by emulsification/internal gelation method".chemical journal of chinese universities-chinese 23.7(2002):1417-1420. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。