The corrosion behaviors of Mg0.9-xTi0.1PdxNi(x=0.04 similar to 0.1) hydrogen storage alloy electrodes
文献类型：期刊论文
| 作者 | Tian, QF; Zhang, Y; Tan, ZC; Sun, LX; Xu, F; Yuan, HT |
| 刊名 | acta physico-chimica sinica
 |
| 出版日期 | 2006-03-01 |
| 卷号 | 22期号:3页码:301-305 |
| 关键词 | hydrogen storage alloys element substitution corrosion potential corrosion current passive film |
| 英文摘要 | the effects of partial substitution of pd for mg on the corrosion behaviors of mg0.9-xti0.1pdxni (x=0.04-0.1) hydrogen storage alloys were studied in this paper. the alloys were prepared by mechanical alloying. the alloy structures became amorphous after ball milling 120 h, which was confirmed by xrd and tem analyses. the cyclic charge-discharge tests showed that the pd addition prolonged the cycle life of the alloys effectively. the corrosion performances of the alloys were investigated by open circuit potential measurements, anodic polarization, electrochemical impedance spectroscopy, and xps experiments. the increase of pd content shifted the alloy corrosion potentials towards more positive values. the initial corrosion currents of the alloys and its increment rates along with cycle number decreased with the increase of pd content in the alloys. the measured electrochemical impedance spectra were fitted well with the proposed equivalent circuit model. the analyses suggested that the thickness and the resistance of passive film on the surface of alloys increased with the increase of pd content in the alloys. the results of xps experiments demonstrated that the addition of pd in the alloys suppressed the oxidation and enhanced the anti-corrosion capabilities of the alloys. when the pd content reached 0.1, the corrosion resistant performances of mg0.9ti0.1pdni(x=0.04-0.1) alloys are the best and the discharge capacity retention rate is the highest. |
| WOS标题词 | science & technology ; physical sciences |
| 类目[WOS] | chemistry, physical |
| 研究领域[WOS] | chemistry |
| 关键词[WOS] | amorphous-alloys ; electrochemical characteristics ; discharge capacities ; ti ; pd ; batteries ; ternary ; mgni ; substitution ; performance |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000236122300009 |
| 公开日期 | 2015-11-17 |
| 源URL | [http://159.226.238.44/handle/321008/140003]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Lab Aerosp Catalysis & New Mat, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China 3.Nankai Univ, Inst New Energy Mat Chem, Tianjin 300071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tian, QF,Zhang, Y,Tan, ZC,et al. The corrosion behaviors of Mg0.9-xTi0.1PdxNi(x=0.04 similar to 0.1) hydrogen storage alloy electrodes[J]. acta physico-chimica sinica,2006,22(3):301-305. |
| APA | Tian, QF,Zhang, Y,Tan, ZC,Sun, LX,Xu, F,&Yuan, HT.(2006).The corrosion behaviors of Mg0.9-xTi0.1PdxNi(x=0.04 similar to 0.1) hydrogen storage alloy electrodes.acta physico-chimica sinica,22(3),301-305. |
| MLA | Tian, QF,et al."The corrosion behaviors of Mg0.9-xTi0.1PdxNi(x=0.04 similar to 0.1) hydrogen storage alloy electrodes".acta physico-chimica sinica 22.3(2006):301-305. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。