Synthesis of nanometer magnesia with high surface area by solid-state chemical reaction
文献类型:期刊论文
作者 | Guan Hongbo; Wang Pei; Zhao Biying; Zhu Yuexiang; Xie Youchang |
刊名 | chinese journal of catalysis |
出版日期 | 2006-09-01 |
卷号 | 27期号:9页码:793-798 |
关键词 | nanometer magnesia oxalic acid magnesium acetate solid-state chemical reaction high surface area |
英文摘要 | nanometer mgo samples with high surface area, small crystal size, and mesoporous texture were synthesized by thermal decomposition of mgc2o4 center dot 2h(2)o, which was prepared by solid-state chemical reaction between h2c2o4 center dot 2h(2)o and mg(ch3coo)(2)center dot 4h(2)o. the existence of steam accelerated the sintering of mgo during the decomposition process and mgo with surface area as high as 412 m(2)/g was obtained through calcining the precursor in flowing dry nitrogen at 520 degrees c for 4 h. the samples were characterized by x-ray diffraction, n-2 adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. the as-prepared mgo was composed of nanocrystals with a size of 4-5 nm and formed a wormhole-like porous structure. in addition, the mgo had good thermal stability, and its surface area was still 357 and 153 m(2) /g after calcination at 600 and 800 degrees c for 2 h, respectively. compared with the mgo sample prepared by the precipitation method, mgo prepared by the solid-state chemical reaction has similar pore size distribution, surface area, and crystal size. the solid-state chemical method has the advantages of low cost, low pollution, and high yield; therefore it appears to be a promising method for the manufacture of nanometer mgo in industry. |
WOS标题词 | science & technology ; physical sciences ; technology |
类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
研究领域[WOS] | chemistry ; engineering |
关键词[WOS] | mgo ; powders |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000241169700010 |
公开日期 | 2015-11-17 |
源URL | [http://159.226.238.44/handle/321008/140103] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | Peking Univ, Coll Chem & Mol Engn, Inst Chem Phys, State Key Lab Struct Chem Unstable & Stable Speci, Beijing 100871, Peoples R China |
推荐引用方式 GB/T 7714 | Guan Hongbo,Wang Pei,Zhao Biying,et al. Synthesis of nanometer magnesia with high surface area by solid-state chemical reaction[J]. chinese journal of catalysis,2006,27(9):793-798. |
APA | Guan Hongbo,Wang Pei,Zhao Biying,Zhu Yuexiang,&Xie Youchang.(2006).Synthesis of nanometer magnesia with high surface area by solid-state chemical reaction.chinese journal of catalysis,27(9),793-798. |
MLA | Guan Hongbo,et al."Synthesis of nanometer magnesia with high surface area by solid-state chemical reaction".chinese journal of catalysis 27.9(2006):793-798. |
入库方式: OAI收割
来源:大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。