The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells
文献类型：期刊论文
| 作者 | Liu Bin1,2; Zhang Yun1,2; Tu Baofeng1,2; Liu Lin1; Dong Yonglai1; Cheng Mojie1 |
| 刊名 | chinese journal of catalysis
 |
| 出版日期 | 2008-10-01 |
| 卷号 | 29期号:10页码:979-986 |
| 关键词 | nickel yttria zirconia reduction electrochemical impedance spectroscopy temperature-programmed reduction solid oxide fuel cell |
| 英文摘要 | the reduction behavior of a sintered nio/ysz anode used for intermediate temperature solid oxide fuel cells was studied by hydrogen temperature-programmed reduction (h-2-tpr). the reduction process of the nio/ysz anode in the cell was in situ monitored by open circuit voltage (ocv) and electrochemical impedance spectroscopy (eis). h-2-tpr results show that the higher sintering temperature of the nio/ysz anode results in a slower reduction of nio to metallic ni. however, when the sintering temperature is elevated to 1500 degrees c, the reduction of sintered nio/ysz anode powder instead becomes easier. the higher nio content in the anode leads to the more rapid reduction of the corresponding anode powder. the above h2-tpr results can be attributed to the combined effects of the growth up of nio particles and the interface separation between nio and ysz caused by the anode sintering. the variation of ocvs reveals that for the cells, the anode with higher nio content has a slower reduction process, which can be ascribed to the retarding effect of excessive h2o produced during the initial reduction period. it was found from the eis results that the 50% nio/ysz anode has a most stable reduction process, whereas for the cells with 30 % and 70 % nio/ysz anodes, both the polarization resistances gradually increase after experiencing an initial decrease for a short period. the cell polarization resistance with 30 % nio/ysz anode keeps no change any more after reduction for 600 min, whereas the cell polarization resistance with 70 % nio/ysz anode increases continuously. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
| 研究领域[WOS] | chemistry ; engineering |
| 关键词[WOS] | steam reforming catalysts ; x-ray-diffraction ; hydrogen ; kinetics ; ysz ; composite ; mechanism ; sofcs ; nio |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000261011000007 |
| 公开日期 | 2015-11-17 |
| 源URL | [http://159.226.238.44/handle/321008/140957]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Liaoning, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu Bin,Zhang Yun,Tu Baofeng,et al. The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells[J]. chinese journal of catalysis,2008,29(10):979-986. |
| APA | Liu Bin,Zhang Yun,Tu Baofeng,Liu Lin,Dong Yonglai,&Cheng Mojie.(2008).The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells.chinese journal of catalysis,29(10),979-986. |
| MLA | Liu Bin,et al."The Reduction Process of a NiO/YSZ Anode for Intermediate Temperature Solid Oxide Fuel Cells".chinese journal of catalysis 29.10(2008):979-986. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。