Hydrogen storage capacity of nickel supported on a metal-organic framework compound under mild conditions
文献类型：期刊论文
| 作者 | Liu Yingya1,2; Zhang Jian1,2; Zeng Julan1,2; Chu Hailiang1,2; Xu Fen1; Sun Lixian1 |
| 刊名 | chinese journal of catalysis
 |
| 出版日期 | 2008-07-01 |
| 卷号 | 29期号:7页码:655-659 |
| 关键词 | nickel metal-organic framework compound supported composite material hydrogen storage capacity impregnation chemical reduction hydrogen reduction |
| 英文摘要 | the traditional impregnation method was used to support nickel ions on the metal-organic framework compound mil-101 (cr(3)f(h(2)o)(2)o[(o(2)c)-c(6)h(4)-(co(2))](3)center dot nh(2)o, n approximate to 5) for the preparation of a ni/mil-101 composite material. with two ways of impregnation (excessive impregnation and incipient wetness impregnation) followed by two ways of reduction (liquid chemical reduction and solid hydrogenation reduction), four ni/mil-101 samples were obtained. the hydrogen storage capacity of the ni/mil-101 samples was measured under mild conditions (25-100 degrees c, 0.01-4 mpa). compared with the original mil-101, ni/mil-101 had high hydrogen storage capacity because of the ni particles supported on mil-101. among these samples, the sample prepared by excessive impregnation followed by liquid chemical reduction exhibited the highest hydrogen storage capacity of 1.02% at 100 degrees c and 4.0 mpa. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
| 研究领域[WOS] | chemistry ; engineering |
| 关键词[WOS] | high h-2 adsorption ; coordination polymer ; surface-area ; inclusion ; spillover ; binding ; mil-101 ; sites ; mof ; zn |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000258484400014 |
| 公开日期 | 2015-11-17 |
| 源URL | [http://159.226.238.44/handle/321008/141190]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Liaoning, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu Yingya,Zhang Jian,Zeng Julan,et al. Hydrogen storage capacity of nickel supported on a metal-organic framework compound under mild conditions[J]. chinese journal of catalysis,2008,29(7):655-659. |
| APA | Liu Yingya,Zhang Jian,Zeng Julan,Chu Hailiang,Xu Fen,&Sun Lixian.(2008).Hydrogen storage capacity of nickel supported on a metal-organic framework compound under mild conditions.chinese journal of catalysis,29(7),655-659. |
| MLA | Liu Yingya,et al."Hydrogen storage capacity of nickel supported on a metal-organic framework compound under mild conditions".chinese journal of catalysis 29.7(2008):655-659. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。