Scandium-Doped La0.8Sr0.2MnO3-delta Cathode Materials for Intermediate-Temperature Solid Oxide Fuel Cells
文献类型：期刊论文
| 作者 | Yue Xiangling1,2; Liu Lin1; Zhang Min1,2; Yang Min1,2; Dong Yonglai1; Cheng Mojie1 |
| 刊名 | chinese journal of catalysis
 |
| 出版日期 | 2009-02-01 |
| 卷号 | 30期号:2页码:95-103 |
| 关键词 | intermediate-temperature solid oxide fuel cell scandium La0.8Sr0.2MnO3-delta composite cathode material scandium oxide oxygen vacancy |
| 英文摘要 | la0.8sr0.2mn1-xscxo3-delta(abbreviated as lsmsx, x = 0, 0.02, 0.05, and 0.1) samples were prepared using a modified pechini method. x-ray diffraction (xrd) and temperature-programmed reduction (h-2-tpr) were carried out to characterize the structure and the reduction behavior of the lsmsx samples. electrochemical evaluation was employed to assess the performance of intemiediate-temperature solid oxide fuel cells (it-sofcs) using lsmsx-based cathode. xrd analysis indicated that the pure perovskite structure could only be obtained at the sintering temperature of 900 degrees c and lower sc doping concentration (x < 0.1). as the increase of sintering temperature and sc doping concentration, the sc2o3 secondary phase tended to segregate from the perovskite structure. the h-2-tpr profiles of lsmsx samples were greatly affected by the sintering temperature. the substitution-induced improvement in reducibility for lsms samples was detected, which might be ascribed to the increases of mn4+ and oxygen vacancies. it can also be found that the increase of sc2o3 separation possibly brought adverse effect to the reducibility of lsms samples. electrochemical evaluation results showed that the performance of the cells with different cathodes was affected by the sc doping concentration, operation temperature, as well as the cathode sintering temperature. in the range of sc doping concentration studied, lsms-based cathode materials showed higher lower-temperature performance than sc free lsm-based materials. this is primarily due to the increase of substitution-induced oxygen vacancies, which improved the electrochemical activity towards oxygen reduction for lsm-based cathode materials. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | chemistry, applied ; chemistry, physical ; engineering, chemical |
| 研究领域[WOS] | chemistry ; engineering |
| 关键词[WOS] | perovskite-type oxides ; composite cathodes ; catalytic combustion ; redox properties ; performance ; sofcs ; ba0.5sr0.5co0.8fe0.2o3-delta ; lamn1-xcuxo3 ; transport ; oxidation |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000264168700005 |
| 公开日期 | 2015-11-17 |
| 源URL | [http://159.226.238.44/handle/321008/141558]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yue Xiangling,Liu Lin,Zhang Min,et al. Scandium-Doped La0.8Sr0.2MnO3-delta Cathode Materials for Intermediate-Temperature Solid Oxide Fuel Cells[J]. chinese journal of catalysis,2009,30(2):95-103. |
| APA | Yue Xiangling,Liu Lin,Zhang Min,Yang Min,Dong Yonglai,&Cheng Mojie.(2009).Scandium-Doped La0.8Sr0.2MnO3-delta Cathode Materials for Intermediate-Temperature Solid Oxide Fuel Cells.chinese journal of catalysis,30(2),95-103. |
| MLA | Yue Xiangling,et al."Scandium-Doped La0.8Sr0.2MnO3-delta Cathode Materials for Intermediate-Temperature Solid Oxide Fuel Cells".chinese journal of catalysis 30.2(2009):95-103. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。