Preparation and characterization of PdxAgy/C electrocatalysts for ethanol electrooxidation reaction in alkaline media
文献类型：期刊论文
| 作者 | Li, Guanglan1,2; Jiang, Luhua1; Jiang, Qian1,2; Wang, Suli1; Sun, Gongquan1 |
| 刊名 | electrochimica acta
 |
| 出版日期 | 2011-09-01 |
| 卷号 | 56期号:22页码:7703-7711 |
| 关键词 | Electrocatalyst Ethanol electrooxidation PdAg alloy degree Particle size Alkaline media |
| 英文摘要 | carbon-supported bimetallic pdag catalysts with pd/ag atomic ratios varying from 4/1 to 1/2 were prepared by an impregnation-reduction method. the impregnated black mixture was treated in h-2/n-2 atmosphere at a temperature varying from 180 to 500 degrees c. the obtained pdxagy/c catalysts were characterized by x-ray diffraction (xrd), transmission electron microscopy (tem), cyclic voltammetry (cv) and chronoamperometry (ca). xrd results show that the lattice constant of pd is dilated, suggesting the formation of pdag alloy. the lattice constant of pd for the pdxagy/c-500 (reduced at 500 degrees c by h-2) increases linearly and the average metal particle size decreases slightly from 6.8 to 5.1 nm with increasing ag fractions from 20% to 67% in the pdag composition. for pdxagy/c catalysts with a certain specific pd/ag atomic ratio, e.g., pd2ag1/c, the dilated lattice constant of pd is independent of the reducing temperature, indicating the alloy degree for the pd2ag1/c-t catalysts is comparable. the average metal particle size for the pd2ag1/c-t catalysts increases from 3.4 to 5.2 nm with h-2 reduction temperature increasing from 180 to 500 degrees c. the potentiodynamic measurements on ethanol electrooxidation reaction (eor) show that the catalytic activities for the pdxagy/c-t catalysts toward the eor are improved by alloying pd with ag. at typical potential of a working fuel cell, e.g., -0.4v vs. hg/hgo, the eor current density presents a volcano shape as a function of the ag fractions in pdag with the maximum occurs at the pd/ag atomic ratios between 2/1 and 3/1. the ca tests show that the pdxagy/c-500 catalysts perform high stability than that of pd/c-500. the improved eor activity for the pdxagy/c-t catalysts, compared with whether pd/c or ag/c catalyst, may possibly be attributed to the formation of pdag alloy and the fitted particle size. (c) 2011 elsevier ltd. all rights reserved. |
| WOS标题词 | science & technology ; physical sciences |
| 类目[WOS] | electrochemistry |
| 研究领域[WOS] | electrochemistry |
| 关键词[WOS] | supported platinum catalysts ; alcohol fuel-cells ; alloy electrocatalysts ; oxygen reduction ; pd/c catalysts ; size analysis ; oxidation ; palladium ; methanol ; oxide |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000295303700039 |
| 公开日期 | 2015-11-17 |
| 源URL | [http://159.226.238.44/handle/321008/142700]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Direct Alcohol Fuel Cell Lab, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Guanglan,Jiang, Luhua,Jiang, Qian,et al. Preparation and characterization of PdxAgy/C electrocatalysts for ethanol electrooxidation reaction in alkaline media[J]. electrochimica acta,2011,56(22):7703-7711. |
| APA | Li, Guanglan,Jiang, Luhua,Jiang, Qian,Wang, Suli,&Sun, Gongquan.(2011).Preparation and characterization of PdxAgy/C electrocatalysts for ethanol electrooxidation reaction in alkaline media.electrochimica acta,56(22),7703-7711. |
| MLA | Li, Guanglan,et al."Preparation and characterization of PdxAgy/C electrocatalysts for ethanol electrooxidation reaction in alkaline media".electrochimica acta 56.22(2011):7703-7711. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。