Preparation of nanocrystalline tio2 thin film at low temperature and its application in dye-sensitized solar cell
文献类型：期刊论文
| 作者 | Tan, Weiwei1,2; Chen, Jinmao1,2; Zhou, Xiaowen1; Zhang, Jingbo1; Lin, Yuan1; Li, Xueping1; Xiao, Xurui1 |
| 刊名 | Journal of solid state electrochemistry
 |
| 出版日期 | 2009-05-01 |
| 卷号 | 13期号:5页码:651-656 |
| 关键词 | Electrophoretic deposition Nanocrystalline tio2 thin film Common pressure hydrothermal treatment Low temperature preparation Dye-sensitized solar cell |
| ISSN号 | 1432-8488 |
| DOI | 10.1007/s10008-008-0605-4 |
| 通讯作者 | Zhang, jingbo(jbzhang@iccas.ac.cn) |
| 英文摘要 | The electrophoretic deposition combined with common pressure hydrothermal treatment was employed to prepare nanocrystalline tio2 thin film from suspension of tetra-n-butyl titanate and p25 at low temperature. the tetra-n-butyl titanate was hydrolyzed and crystallized into anatase to interconnect nanocrystalline tio2 particles and to stick them to a conductive substrate by common pressure hydrothermal treatment to improve the electron transport properties of the deposited thin film. a dye-sensitized solar cell based on tio2 thin film prepared by the low temperature method yielded the conversion efficiency of 6.12%. due to the relative slower electron transport rate in the deposited film, its conversion efficiency was slightly lower than that of the cell with tio2 thin film prepared by the conventional high temperature sintering method. since it is free of high temperature sintering step, this method can be used to prepare nanocrystalline tio2 thin film on plastic polymer conductive substrate for fabrication of flexible dye-sensitized solar cell. |
| WOS关键词 | MANUFACTURING NANOSTRUCTURED ELECTRODES ; CHEMICAL-VAPOR-DEPOSITION ; CATHODIC ELECTRODEPOSITION ; EFFICIENCY ; LAYERS |
| WOS研究方向 | Electrochemistry |
| WOS类目 | Electrochemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:000263429100001 |
| 出版者 | SPRINGER |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2403469 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Zhang, Jingbo |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem, Key Lab Photochem, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tan, Weiwei,Chen, Jinmao,Zhou, Xiaowen,et al. Preparation of nanocrystalline tio2 thin film at low temperature and its application in dye-sensitized solar cell[J]. Journal of solid state electrochemistry,2009,13(5):651-656. |
| APA | Tan, Weiwei.,Chen, Jinmao.,Zhou, Xiaowen.,Zhang, Jingbo.,Lin, Yuan.,...&Xiao, Xurui.(2009).Preparation of nanocrystalline tio2 thin film at low temperature and its application in dye-sensitized solar cell.Journal of solid state electrochemistry,13(5),651-656. |
| MLA | Tan, Weiwei,et al."Preparation of nanocrystalline tio2 thin film at low temperature and its application in dye-sensitized solar cell".Journal of solid state electrochemistry 13.5(2009):651-656. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。