Combustion synthesis of high porosity sic foam with nanosized grains
文献类型：期刊论文
| 作者 | Qiu, J. F.1,2; Li, J. T.1; Smirnov, K. L.3 |
| 刊名 | Ceramics international
 |
| 出版日期 | 2010-08-01 |
| 卷号 | 36期号:6页码:1901-1904 |
| 关键词 | Porosity Sic Combustion synthesis Physical vapor transportation |
| ISSN号 | 0272-8842 |
| DOI | 10.1016/j.ceramint.2010.03.026 |
| 通讯作者 | Li, j. t.(ljt0012@vip.sina.com) |
| 英文摘要 | High porosity silicon carbide (sic) foam with nanosized grains was synthesized by a newly developed process involving two steps: (i) preparation of si/c foam by gel-casting technique and (ii) fabrication of sic foam by combustion si/c foam in nitrogen atmosphere. the as-synthesized sic foam with a high porosity in the range 70-90% exhibited an attractive strength up to 1.6 mpa. sem analysis showed that the foam struts consisted of tightly bonded sic particles with a grain size of 80-300 nm. (c) 2010 elsevier ltd and techna group s.r.l. all rights reserved. |
| WOS关键词 | HIGH-TEMPERATURE SYNTHESIS ; CATALYST SUPPORT ; PROPAGATION |
| WOS研究方向 | Materials Science |
| WOS类目 | Materials Science, Ceramics |
| 语种 | 英语 |
| WOS记录号 | WOS:000280027800021 |
| 出版者 | ELSEVIER SCI LTD |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2413525 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Li, J. T. |
| 作者单位 | 1.Chinese Acad Sci, Tech Inst Phys & Chem, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China 3.Russian Acad Sci, Inst Struct Macrokinet & Mat Sci, Chernogolovka 142432, Russia |
| 推荐引用方式 GB/T 7714 | Qiu, J. F.,Li, J. T.,Smirnov, K. L.. Combustion synthesis of high porosity sic foam with nanosized grains[J]. Ceramics international,2010,36(6):1901-1904. |
| APA | Qiu, J. F.,Li, J. T.,&Smirnov, K. L..(2010).Combustion synthesis of high porosity sic foam with nanosized grains.Ceramics international,36(6),1901-1904. |
| MLA | Qiu, J. F.,et al."Combustion synthesis of high porosity sic foam with nanosized grains".Ceramics international 36.6(2010):1901-1904. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。