Effects of laser polishing on surface morphology and mechanical properties of additive manufactured TiAl components
文献类型：会议论文
| 作者 | Xu, Zifa; Ouyang, Wentai; Liu, Yufan; Jiao, Junke; Liu, Yuezhuan; Zhang, Wenwu |
| 出版日期 | 2020 |
| 会议日期 | OCT 17-20, 2020 |
| 关键词 | MICROSTRUCTURE ALLOY BEHAVIOR FINISH STEEL SHEET |
| 卷号 | 11717 |
| DOI | 10.1117/12.2587455 |
| 英文摘要 | The laser deposition manufacturing (LMD) is a free-form metal deposition process, which allows generating a prototype or small series of near net-shape structures. Despite numerous advantages, one of the most critical issues of the technique is that produced pieces have a deleterious surface finish which requires post machining steps. Mechanical machining method such as milling and grinding has been used to improve the surface quality of the laser additive manufacturing components. However, the mechanical machining method has some drawbacks such as tool wearing and narrow-area difficult to machining. In this paper, we demonstrate the capability of continuous wave (CW) in polishing rough surface of additive manufactured TiAl alloy. The surface morphology, microstructures, corrosion resistance, micro-hardness and wear resistance of samples were characterized using a laser confocal microscopy (OM), scanning electron microscope (SEM), electrochemical analyzer, Vickers hardness machine, and wear tester, respectively. Results revealed that the surface roughness more than 16.06 mu m could be reduce to less than 1.76 mu m through laser polishing process. It was also found that a hardened layer about 600 mu m was produced on the TiAl alloy surface after laser finishing. The microhardness of the sample was improved about 8% compared with the mechanical milling method. |
| 会议录出版者 | Proceedings of SPIE |
| 学科主题 | Optics ; Physics |
| ISSN号 | 0277-786X |
| ISBN号 | 978-1-5106-4270-6 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/23271]  |
| 专题 | 会议专题 会议专题_会议论文 |
| 推荐引用方式 GB/T 7714 | Xu, Zifa,Ouyang, Wentai,Liu, Yufan,et al. Effects of laser polishing on surface morphology and mechanical properties of additive manufactured TiAl components[C]. 见:. OCT 17-20, 2020. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。