Mechanical properties of SiC fibers irradiated by swift heavy ions
文献类型:会议论文
作者 | Zhang, L. Q.; Zhang, C. H.; Huang, Q.; Yan, T. X.; Ding, Z. N.; Zhang, X. L.; Chen, Y. G.; Ma, B. S.; Li, J. Y. |
出版日期 | 2019 |
会议日期 | DEC 07-08, 2018 |
关键词 | FLOW CHANNEL INSERT DAMAGE |
卷号 | 544 |
DOI | 10.1088/1757-899X/544/1/012015 |
英文摘要 | Mechanical properties and surface features of SiC fibers irradiated with 246.8-MeV Ar ions at different fluences (1.5x10(14), 9.0x10(14), 1.8x10(15), and 2.7x10(15) ions/cm(2)) were investigated using a specific single filament tensile test and a field emission scanning electron microscopy (FE-SEM). Results reveal that carbon concentration on the fiber surface decreases while silicon concentration increases, with increasing ion fluence, accompanied by an adsorption of oxygen. Meanwhile, the diameter of fibers first reduces and then increases, with increasing ion fluence. Moreover, at 2.7x10(15) Ar ions/cm2 irradiation, some fibers were fractured. As a result, the mean tensile strength and the average elastic modulus of fibers decrease generally with respect to the ion fluence. The degradation mechanisms of mechanical properties of SiC fibers under irradiation were discussed in detail. |
会议录出版者 | IOP Conference Series-Materials Science and Engineering |
学科主题 | Engineering ; Materials Science |
ISSN号 | 1757-8981 |
源URL | [http://ir.nimte.ac.cn/handle/174433/23318] |
专题 | 会议专题 会议专题_会议论文 |
推荐引用方式 GB/T 7714 | Zhang, L. Q.,Zhang, C. H.,Huang, Q.,et al. Mechanical properties of SiC fibers irradiated by swift heavy ions[C]. 见:. DEC 07-08, 2018. |
入库方式: OAI收割
来源:宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。