Influence of Nitrogen Partial Pressure on the Microstructure and Properties of TiN Coatings
文献类型：会议论文
| 作者 | Xie, Shifang; Liu, Keming; Ke, Peiling; Zhang, Dong; Wei, Shiyong; Wang, Aiying |
| 出版日期 | 2014 |
| 会议日期 | AUG 23-24, 2014 |
| 关键词 | TITANIUM |
| 卷号 | 1049 |
| DOI | 10.4028/www.scientific.net/AMR.1049-1050.89 |
| 英文摘要 | TiN coatings were prepared by using multi-arc ion plating technique at different N-2 partial pressures. The surface morphology of the coatings was characterized by using a tabletop scanning electron microscope. The cross-sectional microstructure was investigated by using a field emission scanning electron microscope. The phase composition was evaluated by using an X-Ray diffractometer. The hardness and cohesion were measured by using a nano indentation tester and a scratch instrument, respectively. The results show that the number and size of macro-particles decrease and the compactness of TiN coating increases with the increase of the N-2 partial pressure. The hardness and cohesion of the coating increase gradually with increasing N-2 partial pressures and reach a peak at 0.6 Pa; then the hardness and cohesion are significantly lower at higher N-2 partial pressures. |
| 会议录出版者 | Advanced Materials Research |
| 学科主题 | Materials Science |
| ISSN号 | 1022-6680 |
| ISBN号 | 978-3-03835-314-0 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/23536]  |
| 专题 | 会议专题 会议专题_会议论文 |
| 推荐引用方式 GB/T 7714 | Xie, Shifang,Liu, Keming,Ke, Peiling,et al. Influence of Nitrogen Partial Pressure on the Microstructure and Properties of TiN Coatings[C]. 见:. AUG 23-24, 2014. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。