Coercivity Enhancement of HDDR Hot-Pressed Magnets by NdCu Diffusion Treatment
文献类型：会议论文
| 作者 | Cai, Lingwen; Guo, Shuai; Yan, Changjiang; Zhang, Xiaofeng; Chen, Renjie; Liu, Lidong; Lee, Don; Yan, Aru |
| 出版日期 | 2014 |
| 会议日期 | MAY 04-08, 2014 |
| 关键词 | FE-B POWDERS MICROSTRUCTURE |
| 卷号 | 50 |
| 期号 | 11 |
| DOI | 10.1109/TMAG.2014.2326715 |
| 英文摘要 | In order to improve the coercivity of hot-pressed magnets with hydrogenation disproportionation desorption recombination (HDDR) powders being the precursor, diffusion processing of an NdCu eutectic alloy is employed for grain boundary modification, resulting in an increase of coercivity from 15.4 to 17.8 kOe, which leads to a better thermal stability with the temperature coefficient (beta) changing from -0.549%/K to -0.519%/K. It is evidently observed that Nd-rich grain boundary layers are formed between the adjacent matrix phase grains as well as in the junction parts after diffusion treatment, which is responsible for the coercivity enhancement of the HDDR hot-pressing magnets. The influence of the microstructure on the coercivity has been further investigated to reveal that the Nd-rich phases occurred during the boundary modification process of the NdCu eutectic alloy decouple the exchange interactions between the grains. |
| 学科主题 | Engineering ; Physics |
| ISSN号 | 0018-9464 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/23540]  |
| 专题 | 会议专题 会议专题_会议论文 |
| 推荐引用方式 GB/T 7714 | Cai, Lingwen,Guo, Shuai,Yan, Changjiang,et al. Coercivity Enhancement of HDDR Hot-Pressed Magnets by NdCu Diffusion Treatment[C]. 见:. MAY 04-08, 2014. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。