Synthesis and Physical Properties of Graphene Nanosheets Reinforced Copper Composites
文献类型：会议论文
| 作者 | Wei, Bingwei; Qu, Dong; Hu, Chunfeng; Li, Fangzhi; Zhou, Tianliang; Xie, Rongjun; Zhou, Zhiming |
| 出版日期 | 2014 |
| 会议日期 | JUL 23-25, 2013 |
| 关键词 | MECHANICAL-PROPERTIES |
| 卷号 | 833 |
| DOI | 10.4028/www.scientific.net/AMR.833-310 |
| 英文摘要 | Cu/gaphene nanosheets composites were fabricated at 800 degrees C by the hot-pressing method using Cu and graphene as initial materials. Graphene content was 1 wt. %-5 wt. %. The fracture morphology and physical properties of the composites were investigated. It was found that the relative density increased with the increment of graphene content from 1 wt% to 5 wt. % with reaching its highest level (96.68%) at 5wt. %. The composites have the anisotropic property which is vertical to the direction of pressure is higher than parallel to the direction of pressure. With the increasing of graphene content, the thermal conductivity property and the electronic conductivity decrease first and then increase with the minimum thermal conductivity and electric conductivity at 3wt /0 similar to 4wt%. |
| 会议录出版者 | Advanced Materials Research |
| 学科主题 | Materials Science |
| ISSN号 | 1022-6680 |
| ISBN号 | 978-3-03785-919-3 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/23563]  |
| 专题 | 会议专题 会议专题_会议论文 |
| 推荐引用方式 GB/T 7714 | Wei, Bingwei,Qu, Dong,Hu, Chunfeng,et al. Synthesis and Physical Properties of Graphene Nanosheets Reinforced Copper Composites[C]. 见:. JUL 23-25, 2013. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。