Effect of Rare-Earth Content on Coercivity and Temperature Stability of Sintered Nd-Fe-B Magnets Prepared by Dual-Alloy Method
文献类型：会议论文
| 作者 | Fu, Wenbiao; Guo, Shuai; Lin, Chaowei; Chen, Renjie; Liu, Xincai; Lee, Don; Yan, Aru |
| 出版日期 | 2013 |
| 会议日期 | JAN 14-18, 2013 |
| 关键词 | PERMANENT-MAGNETS NDFEB MICROSTRUCTURE |
| 卷号 | 49 |
| 期号 | 7 |
| DOI | 10.1109/TMAG.2013.2252156 |
| 英文摘要 | The influence of rare earth content on coercivity and temperature stability with dual-alloy method has been investigated. It is found that the coercivity of magnets increases rapidly firstly and then slightly with the increasing of rare earth content from the range of 29.5 wt% to 33.5 wt%. The coercivity and the temperature coefficient of coercivity will get better with rare earth content of 31.5 wt%. The result of magnetic anisotropy field of magnet revealed that it almost has no change with different rare-earth content. Scanning electron microscopy (SEM) and Transmission electron microscope (TEM) revealed that continuous thin layers of Nd-rich phase about 4 nm were found along the grain boundaries in the annealed sample at 31.5 wt% rare earth content, while the grain boundary width of magnet exceeds 8 nm at 33.5 wt%. |
| 学科主题 | Engineering ; Physics |
| ISSN号 | 0018-9464 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/23608]  |
| 专题 | 会议专题 会议专题_会议论文 |
| 推荐引用方式 GB/T 7714 | Fu, Wenbiao,Guo, Shuai,Lin, Chaowei,et al. Effect of Rare-Earth Content on Coercivity and Temperature Stability of Sintered Nd-Fe-B Magnets Prepared by Dual-Alloy Method[C]. 见:. JAN 14-18, 2013. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。