The microstructure and magnetization behaviors of (Pr8.2Fe86.1-xCoxB5.7)(0.99)Zr-0.01 (x=0-10) nanocomposite magnets
文献类型:会议论文
作者 | Chen, Renjie; Guo, Shuai; Wang, Jinzhi; Lee, Don; Yan, Aru |
出版日期 | 2011 |
会议日期 | NOV, 2010 |
关键词 | PERMANENT-MAGNETS |
卷号 | 109 |
期号 | 7 |
DOI | 10.1063/1.3566074 |
英文摘要 | Nanocomposite (Pr8.2Fe86.1-xCoxB5.7)(0.99)Zr-0.01 (x = 0-10) ribbons consisting of Pr-2(Fe,Co)(14)B and alpha-(Fe,Co) phases were prepared by a melt-spun technique. The microstructure and magnetic properties were studied. The results show that the Curie temperature increases drastically with increasing Co content. The optimal permanent magnetic properties are obtained at x = 2, and the value of H-ci, M-s, M-r, and (BH)(max) are 6.52 kOe, 150.2 emu/g, 120.9 emu/g, and 22.34 MGOe, respectively. Typical magnetization behaviors of nanocomposite magnets are found in these ribbons. The significant remanence enhancement indicates that a strong intergrain exchange coupling exists in all ribbons studied in this work. By Co substitution, the intergrain exchange coupling is enhanced significantly. The study of microstructure shows that the larger grains of Pr-2(Fe,Co)(14)B hard phase are surrounded by the smaller grains of alpha-(Fe,Co) soft phase with size about 10-20 nm in the ribbon with Co substitution. This kind of microstructure is in favor of exchange coupling between magnetically hard and soft phases and results in excellent magnetic properties. (c) 2011 American Institute of Physics. [doi:10.1063/1.3566074] |
学科主题 | Physics |
ISSN号 | 0021-8979 |
源URL | [http://ir.nimte.ac.cn/handle/174433/23692] |
专题 | 会议专题 会议专题_会议论文 |
推荐引用方式 GB/T 7714 | Chen, Renjie,Guo, Shuai,Wang, Jinzhi,et al. The microstructure and magnetization behaviors of (Pr8.2Fe86.1-xCoxB5.7)(0.99)Zr-0.01 (x=0-10) nanocomposite magnets[C]. 见:. NOV, 2010. |
入库方式: OAI收割
来源:宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。